Abstract:<p>Carbon/carbon (C/C) composites have a wide application as the thermal structure materials because of their excellent properties at high temperatures. However, C/C composites are easily oxidized in oxygen-containing environment, which limits their potential applications to a great degree. Silicon carbide (SiC) ceramic coating fabricated via pack cementation (PC) was considered as an effective way to protect C/C composites against oxidation. But the mechanical properties of C/C composites were severely damaged due to chemical reaction between the molten silicon and C/C substrate during the preparation of SiC coating by PC. In order to eliminate the siliconization erosion, a pyrolytic carbon (PyC) coating was pre-prepared on C/C composites by the chemical vapor infiltration (CVI) prior to the fabrication of SiC coating. Due to the retardation effect of PyC coating on siliconization erosion, the flexural strength retention of the SiC coated C/C composites with PyC coating increased from 46.27 % to 107.95 % compared with the specimen without PyC coating. Furthermore, the presence of homogeneous and defect-free PyC coating was beneficial to fabricate a compact SiC coating without silicon phase by sufficiently reacting with molten silicon during PC. Therefore, the SiC coated C/C composites with PyC coating had better oxidation resistances under dynamic (between room temperature and 1773 K) and static conditions in air at different temperatures (1773-1973 K).</p>

Improvement of the Bonding Strength and the Oxidation Resistance of SiC Coating on C/C Composites by Pre-Oxidation Treatment

Oxidation Pre-Treatment to Improve the Mechanical Property and Oxidation Resistance of Si–Mo–Cr Coated C/C Composites

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

Interfacial modification and oxidation resistance behavior of a CVD-SiC coating for C/SiC composites

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer

Effect of Al2O3 addition on the microstructure and oxidation behavior of SiC coating prepared by pack cementation on C/C composites

Oxidation protection and behavior of C/C composites with an in situ SiC nanowire-SiC-Si/SiC-Si coating

SiCn/SiC Oxidation Protective Coating for Carbon/carbon Composites

Oxidation Protection of C/C Composites by Ultra Long SiC Nanowire-Reinforced SiC–Si Coating

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

Effect of heat-treatment on the oxidation resistance of Mo-Si-N coating for C/C composites

Effect of SiC Nanowires on the Mechanical and Oxidation Protective Ability of SiC Coating for C/C Composites

Siliconization elimination for SiC coated C/C composites by a pyrolytic carbon coating and the consequent improvement of the mechanical property and oxidation resistances

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Microstructure and Oxidation Resistant Property of C/C Composites Modified by SiC–MoSi2–CrSi2 Coating

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

Bamboo-shaped SiC Nanowire-Toughened SiC Coating for Oxidation Protection of C/C Composites

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

A Chromium Carbide Coating In-Situ Formed on C/C Composites by the Novel Reactive Wetting Strategy to Enhance Oxidation Resistance