Abstract:The deposition of ternary nitrides with the incorporation of carbon atoms into its structure has demonstrated to be a promising approach in the pursuit of wear-resistant and self-lubricating coatings. Firstly, both TiAlN and TiAlCN monolayers were deposited using direct current magnetron sputtering (DCMS) and high-power impulse magnetron sputtering (HiPIMS) onto quenched and tempered AISI H11 tool steel to be used as references. Acetylene was used as a carbon precursor, producing DCMS and HiPIMS TiAlCN coatings with 9.0 and 21.7 at.% C, respectively.Subsequently, TiAlN/TiAlCN multilayers of various designs were also developed as follows: 5×[10/500], 5×[50/500] and 5×[100/500] nm. Residual stresses of the coating systems were determined by X-ray radiation utilising an ETA-diffractometer with a Cu-Kα radiation source applying the sin2ψ method. Additionally, residual stresses depth gradients of the substrate before and after the deposition of the coatings were determined in a LEDDI 8-circle diffractometer equipped with a W-X-ray tube and operated in the energy-dispersive mode of diffraction. Great reduction of the compressive residual stresses in the coatings was observed after the introduction of carbon into the TiAlN coating structure, shifting from −1047 ± 149 to −307 ± 211 MPa for the DCMS and from −7035 ± 1361 to +989 ± 187 MPa for the HiPIMS coatings. In the multilayer coatings, compressive residual stresses increase along with the increment of the TiAlN interlayer. Additionally, residual stresses of the substrate in the near-surface are dragged from low compressive stresses (−218 ± 61) to tensile stresses in the range of 1000 to 2000 MPa for all the DCMS/substrate systems, a behaviour only presented in HiPIMS by the TiAlN monolayer. Wear coefficients of all the evaluated HiPIMS systems are notoriously lower than their DCMS counterparts. Compared to TiAlN, TiAlCN HiPIMS presented a lower coefficient of friction but a higher wear coefficient, which in turn was not reduced by the introduction of the multilayer systems. Finally, Scratch test and Rockwell C adhesion tests have shown higher adhesion of DCMS coatings than HiPIMS coatings, and a detriment of the monolayers adhesion by the implementation of TiAlN/TiAlCN multilayer systems. The understanding of the residual stresses, both in the coating and in the substrate, and the way they affect the tribomechanical performance of the system coating/substrate continues to be of great importance, especially for coatings deposited by new technologies such as HiPIMS and self-lubricating coatings.

Structure, adhesion and corrosion behavior of CrN/TiN superlattice coatings deposited by the combined deep oscillation magnetron sputtering and pulsed dc magnetron sputtering

Structure, Mechanical and Tribological Properties of Self-Toughening TiSiN/Ag Multilayer Coatings on Ti6Al4V Prepared by Arc Ion Plating

Structure, mechanical and tribological properties of thick CrNx coatings deposited by HiPIMS

Improving the adhesion of CrN coatings on TC4 alloy substrates by discharge current modulation in magnetron sputtering

Microstructure and Tribological Behavior of TiAlSiN Coatings Deposited by Deep Oscillation Magnetron Sputtering

Microstructure and mechanical properties of nano-multilayer structured (AlCrMoTaTi)Nx coatings deposited by closed field unbalanced magnetron sputtering

Fabrication and Performance of TiN/TiAlN Nanometer Modulated Coatings

Structural and Mechanical Properties of Multi-Element (alcrmotatizr)nx Coatings by Reactive Magnetron Sputtering

Interface Feature via Key Factor on Adhesion of CrN Multilayer and Alloy Substrate

Structure and mechanical properties of graded Cr/CrN/CrTiN coatings synthesized by close field unbalanced magnetron sputtering

The microstructure and mechanical properties of Ti(CoCr)N films produced by DC magnetron sputtering

Role of atomic layer deposited TiOxNy interlayer in tribological and corrosion properties of CrN coating

Microstructure, mechanical and tribological properties of CrN/W2N multilayer films deposited by DC magnetron sputtering

Bilayer period and ratio dependent structure and mechanical properties of TiN/MoNx superlattices

Microstructure, Adhesion and Tribological Properties of CrN/CrTiAlSiN/WCrTiAlN Multilayer Coatings Deposited on Nitrocarburized AISI 4140 Steel

Mechanical properties, thermal stability and oxidation resistance of TiN/CrN multilayer coatings

Microstructure, Tribocorrosion and Corrosion Performances of Laser Cladded Ni625-xTiC Coatings in 3.5% NaCl Solution

(AlCrNbSiTi)N/TiN multilayer films designed by a hybrid coating system combining high-power impulse magnetron sputtering and cathode arc deposition

Residual stresses and tribomechanical behaviour of TiAlN and TiAlCN monolayer and multilayer coatings by DCMS and HiPIMS

Investigation Of The Oxidation Mechanisms Of Superlattice Cr-Crn/Tisin-Cr Multilayer Coatings On Zircaloy Substrates Under High-Temperature Steam Atmospheres

Structure and fracture toughness of TiAlN thin films deposited by deep oscillation magnetron sputtering