Abstract:This present article deals with bending deformation and failure behavior of sandwich and multilayer beams composed of aluminum foam core and metallic face sheets analyzed by in-situ surface displacement analysis (SDA). The effect of beam structure on the failure mode of beam and the energy absorbed by beam failure were investigated and discussed. The SDA results revealed that collapse of the sandwich beams is by two basic modes, indentation (ID) and core shear (CS). The ID is localized deformation on the beam adjacent to the inner or outer roller in four-point bending, where displacement and compressive strains are at the maximum. As for CS mode, failure occurs in the core between inner and outer rollers, which corresponds to the maximum shear strain; discontinuous displacements in both the vertical and horizontal directions are the primary factors for shear crack initiation, growth, and broadening. The failure of the multilayer beams depends on whether the face sheets show ID mode or otherwise. If a single layer core sandwich fails in ID mode, the multilayer beams with similar face sheets show mixed ID + CS modes. If a single layer core sandwich fails fully in CS mode, no ID characteristic appears in the similar face sheet multilayer beams. The deformation energy of the beams relates strongly to the structure and geometry of beam. The predication of the bending fracture work W x of a beam is given by W_x /W_5 = 0.3875C + 0.9383 where W 5 is the deformation energy of the beam with a 5-mm core, and C is the thickness ratio of the core x to 5 mm.

Failure Mechanism of Sandwich Beams Subjected to Three-Point Bending

Failure Analysis of Sandwich Beams under Three-Point Bending Based on Theoretical and Numerical Models

The Failure Behavior of Double-Layer Metal Foam Sandwich Beams under Three-Point Bending

Three-point Bending of Physically Asymmetric Metal Sandwich Beams with Aluminum Foam Core: Failure Behavior and Optimal Design

The Failure Behavior of Geometrically Asymmetric Metal Foam Core Sandwich Beams under Three-Point Bending

Static and Low-Velocity Impact Behavior of Sandwich Beams with Closed-Cell Aluminum-Foam Core in Three-Point Bending

Analysis of deformation and failure mechanism of sandwich beams with lattice core under three-point bending load

Deformation and Failure Mechanisms of Sandwich Beams under Three-Point Bending at Elevated Temperatures

Three-point bending of sandwich beams with aluminum foam-filled corrugated cores

Modeling and Failure Analysis of Elastic-plastic Sandwich Beams

The Load-Carrying Capacity of Sandwich Beams in Different Collapse Mechanisms

Failure Behavior of a Sandwich Beam with GLARE Face-Sheets and Aluminum Foam Core under Three-Point Bending

Structural Design of Pyramidal Truss Core Sandwich Beams Loaded in 3-Point Bending

Bending Response of Carbon Fiber Composite Sandwich Beams with Three Dimensional Honeycomb Cores

Indentation of sandwich beams with metal foam core

Three-point bending behaviors of the foam-filled CFRP X-core sandwich panel: Experimental investigation and analytical modelling

Responses of Damage and Energy of Sandwich and Multilayer Beams Composed of Metallic Face Sheets and Aluminum Foam Core under Bending Loading

Failure behavior and damage model of composite sandwich panels under three-point bending fatigue load

EXPERIMENT AND THEORETICAL ANALYSIS ON FLEXURAL FAILURE MODE OF COMPOSITE SANDWICH BEAMS

Failure Mode of Aluminum Foam-Filled Corrugated Sandwich Beam Under Three-Point Bending Load

Deformation and Failure of Hybrid Composite Sandwich Beams with a Metal Foam Core under Quasi-Static Load and Low-Velocity Impact