Application of High Velocity Oxygen Fuel Flame (HVOF) Spraying to Fabrication of La0.8Sr0.2Ga0.8Mg0.2O3 Electrolyte for Solid Oxide Fuel Cells

Shan-Lin Zhang,Cheng-Xin Li,Chang-Jiu Li,Guan-Jun Yang,Meilin Liu

DOI: https://doi.org/10.1016/j.jpowsour.2015.09.050

IF: 9.2

2015-01-01

Journal of Power Sources

Abstract:La0.8Sr0.2Ga0.8Mg0.2O3 (LSGM) is considered a promising electrolyte for intermediate-temperature solid oxide fuel cells (IT-SOFCs) due to its high ionic conductivity and stability under fuel cell operating conditions. Here we report our findings in investigating the feasibility of using a high velocity oxygen fuel flame (HVOF) spraying process for cost-effective fabrication of dense LSGM electrolyte membranes. The flame and in-flight particle behavior were simulated numerically to optimize the microstructure and phase compositions of the LSGM deposits. The measured gas leakage rate of an LSGM deposit is similar to 7 x 10(-7) cm(4)gf(-1) s(-1). The single cell assembled with 50-55 mu m HVOF-sprayed LSGM electrolyte shows open circuit voltage (OCV) of 1.08 V at 800 degrees C, suggesting that the as-sprayed LSGM deposit is dense enough for direct application as SOFC electrolyte. At 800 degrees C, the ionic conductivity of the sprayed LSGM deposit is similar to 0.04 S cm(-1), indicating that the HVOF spraying is a promising process for low-temperature fabrication of dense LSGM electrolyte membranes for IT-SOFCs. (C) 2015 Elsevier B.V. All rights reserved.