Abstract:The oxidation behavior and oxidation products of hot-pressed ZrB2-SiC ceramic composites are investigated under plasma conditions in the high temperature, low pressure partially dissociated oxygen stream of the home-made dissociated oxygen simulation set-up. Specimens are oxidized at different environments for exposure time of 30 min at surface temperatures ranging from 1000 °C to 1800 °C. The microstructures and composition of the oxide scale are characterized using environment scanning electron microscopy, x-ray diffraction, and energy-dispersive spectroscopy analysis, and the weight change is also measured. Consistent with the surface reaction and volatility diagram, the curve of the weight change could be divided into four stages. Comparison is made with specimens oxidized under similar temperature and pressure conditions in oxygen environment in which atomic oxygen concentrations are negligible. Both of active oxidation and passive oxidation uptake of the specimens are observed with silicon oxide and silicate formation. The results indicate that the active oxidation is found to have remarkable effect on phase composition of the surface oxide scale, and the oxidation behavior of hot-pressed ZrB2-SiC ceramic composites changes under dissociated oxygen.

Effects of Oxygen Partial Pressure on the Oxidation of ZrB2–SiC–graphite Composites at 1800 °C

Oxidation of ZrB2–SiC‐Graphite Composites under Low Oxygen Partial Pressures of 500 and 1500 Pa at 1800°C

Effects of Oxygen Partial Pressure and Atomic Oxygen on the Microstructure of Oxide Scale of ZrB2–SiC Composites at 1500 °C

Effects of Oxidation Temperature, Time, and Ambient Pressure on the Oxidation of ZrB2–SiC–graphite Composites in Atomic Oxygen

Oxidation Behaviour of Zirconium Diboride–silicon Carbide Ceramic Composites under Low Oxygen Partial Pressure

Effect of atomic oxygen on oxidation behavior of ZrB2-SiC ceramic composite materials

Oxidation Behaviors of C–ZrB2–SiC Composite at 2100 °C in Air and O2

High temperature oxidation resistance of hot-pressed h-BN/ZrO 2 composites

OXIDATION OF ZIRCONIUM DIBORIDE-SILICON CARBIDE CERAMIC COMPOSITES IN DISSOCIATED OXYGEN

Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites: Oxidation Behaviors of the Pressureless Sintered ZrB<SUB>2</SUB>-SiC Composites

Oxidation Behavior of ZrB2–SiC–ZrO2 Ceramic Composites in the Temperature Range of 800–1200°C

Oxidation behavior of zirconium diboride–silicon carbide at 1800°C

Oxidation Properties of ZrB2-20vol.%SiC-10vol.%BN Ceramic Composite at 1200°C

Oxidation Kinetics of Hot-Pressed ZrB2–SiC Ceramic Matrix Composites

Oxidation-resistant ZrB2–SiC composites at 2200°C

Oxidation Behaviour of C–SiC–ZrC Composite

Oxidation Behavior of ZrC-based Composites in Static Laboratory Air Up to 1300 °C

Oxidation of ZrC-30vol% SiC composite in air from low to ultrahigh temperature

Atomic oxygen adsorption and its effect on the oxidation behaviour of ZrB2–ZrC–SiC in air

Oxidation of Zirconium Diboride–silicon Carbide Ceramics under an Oxygen Partial Pressure of 200 Pa: Formation of Zircon

High-Temperature Oxidation Resistance of ZrB2-SiC Ceramic Composites Prepared by Reactive Hot Pressing