Preparation and Properties of Anorthite‐based Ceramics by Using Metallurgical Solid Waste and Fly Ash
Can Shen,Yilun Huang,Yuena Zhang,Xiaowen Wu,Tianyi Tao,Xin Min,Zhaohui Huang,Minghao Fang,Yangai Liu,Ruiyu Mi
DOI: https://doi.org/10.1111/ijac.14337
2023-01-01
International Journal of Applied Ceramic Technology
Abstract:A large amount of metallurgical solid waste accumulation poses a serious threat to the environment. Study on synergistic reinforcement of synthetic process of metallurgical solid waste-based ceramics with fly ash is of great significance in reducing environmental pollution and resource utilization. A metallurgical solid waste-based ceramic used as building ceramic was developed with the erosion part of used MgO-C bricks and fly ash as main raw materials, and the amount of solid waste added to the prepared ceramics was at least 60 wt% and up to 90 wt%. The effects of fly ash content and sintering temperature on the crystalline phase transitions, morphologies, and the main physical and mechanical properties of ceramics were investigated by X-ray diffraction, scanning electron microscopy, and mechanical testing. The results show that the obtained ceramics presented maximum bending strength and minimum water absorption, 80.14 MPa and 5.04%, respectively, when the raw material proportions were the erosion part of used refractories accounted for 60 wt%, fly ash 20 wt%, pyrophyllite 10 wt%, and quartz sands 10 wt%, and the process parameters were the sintering temperature 1150 degrees C, sintering time 120 min, and molding pressure 15 MPa.