Abstract:Fiber reinforced ceramic matrix composites (CMCs) are widely investigated in recent years in order to obtain their damage mechanisms, failure modes and mechanical properties. A well-accepted fact is that the interface between the fibers and the ceramic matrix has great effects on the mechanical behavior of CMCs. The tough and nonlinear stress-strain behavior of CMCs can mainly be attributed to matrix cracking and interface debonding. Therefore, how these two factors affect the stress-strain relationship and the final strength of CMCs needs to be deeply studied. In this paper, the damage evolution and the tensile stress-strain behavior of 2D-C/SiC composite were investigated under monotonic and stepwise incremental loadings and unloadings. The strain is measured by 25 mm extensometer. The experimental results show that the stress-strain behavior of the material is obviously nonlinear; the unloading modulus decreases while the inelastic strain increases with increasing of the unloading stress; the relational curves of residual strain and unloading modulus versus the applied stress have analogous form with the tensile stress-strain curve; the fracture of the composite is quasi-brittle, i.e. catastrophic. Based on the shear-lag theory and the rule of mixture, a concise constitutive equation and a tensile strength calculation model of the damaged material were established. The simulated stress-strain curve is in good agreement with the experimental data when the applied stress is lower than 100 MPa. The difference between the theoretical curve and the experimental data when the applied stress is higher than 100 MPa mainly comes from the local strain concentrations within the seriously damaged zone, because large crack openings usually appear in this region from the experimental view. The analysis results reveal that the residual strain mainly depends on the crack opening displacement and the crack spacing, while the unloading modulus is significantly dependent on the interface debonding rate. Moreover, the uniaxial tensile behavior of 2D-C/SiC composite is mostly dominated by the longitudinal fiber bundles; the contributions of transverse fibers to the material's modulus and strength are obviously small. In the strength model, the failure criteria proposed by Tsai-Hill was applied to obtain the off-axes strength, and then the curved fiber bundle in the real material structure was equivalent to the straight. Furthermore, the rule of mixture was modified and the expression for strength calculation was presented. And, the predicted tension strength ranges from 210.5 MPa to 265.6 MPa for the 2D-C/SiC composite with 0.15 μm thick carbon interphase, which is also in good agreement with the experimental data.

In-plane Shear Behaviours of a 2D-Sic/sic Composite under Various Loading Conditions

In-plane Mechanical Behavior and Failure Mode of a 2D-Sic/sic Composite under Uniaxial Dynamic Compression

Effect of Shear Strain Rate on Interlaminar Shear Behavior of 2D-C/sic Composites: A Damage Transition from Notch Ends Initiation to Gauge Section Initiation

Mechanical Behavior and Failure Mechanism of 2D-Sicf/sic Composite under Dynamic Tensile Loading Through Experimental and Numerical Investigation

Infrared Thermography For Non-Destructive Evaluation Of 2d C/Sic Composites Under Fatigue Loading

Damage Characteristics and Constitutive Modeling of the 2D C/SiC Composite: Part I – Experiment and Analysis

Application and Analysis of Plane Woven C/Sic Composites Based on Continuum Damage Mechanics

Cross-scale Static/dynamic Shear Damage Evolution Mechanism of 2D C/SiC Ceramic Matrix Composite with Transient Hysteresis Effect

Infrared Thermography and Acoustic Emission in 2D Plain Woven C/Sic Composites under Tensile-Tensile Fatigue Loading

Damage Theoretical Analysis of 2.5D C/SiC Composites under Tensile and Shear Loading

Experimental Investigation on Interlaminar and In-Plane Shear Damage Evolution of 2D C/SiC Composites Using Acoustic Emission and X-ray Computed Microtomography

Transition of in-plane compressive strength and failure mechanism of 2D-C/SiC: Influence of off-axis loading angle and loading rate

Uniaxial tensile stress-strain behavior and strength of plain woven C/SiC composite

Interlaminar Shear Damage Mechanisms of a 2D-C/sic Composite at Elevated Temperature in Vacuum

Poisson Effects of 2D-C/sic Composite under Axial Loading Conditions

Failure and Strength of 2D-C/sic Composite under In-Plane Shear Loading at Elevated Temperatures

Characterisation and analysis of the damage coupling effects of a 2D-C/SiC composite under proportional loading conditions

DAMAGE EVOLUTION AND MICROSTRUCTURAL CHARACTERIZATION OF A CROSS-WOVEN C/SiC COMPOSITE UNDER TENSILE LOADING

Uniaxial Macro‐Mechanical Property and Failure Analysis of a 2D‐Woven SiC/SiC Composite

Comparison of in-plane shear behaviors of 2-d plain woven C/SIC composites

In-plane Shear Performance Statistics of 2D-C/sic Composites and Its B-basis Value of Strength