Co1−xMgxFe2O4 Magnetic Particles: Preparation and Kinetics Research of Thermal Transformation of the Precursor

Qin Liqin,Gao Minlin,Wu Wenwei,Ou Shiqian,Wang Kaituo,Liu Bang,Wu Xuehang
DOI: https://doi.org/10.1016/j.ceramint.2014.03.079
IF: 5.532
2014-01-01
Ceramics International
Abstract:Co1−xMgxFe2O4 precursor was synthesized by solid-state reaction at low temperatures using MgSO4·7H2O, CoSO4·7H2O, FeSO4·7H2O, and Na2C2O4 as raw materials. Co1−xMgxFe2O4 was obtained by calcining the precursor over 500°C in air. The precursor and its calcined products were characterized by thermogravimetry and differential scanning calorimetry, X-ray powder diffraction, scanning electron microscopy, and vibrating sample magnetometry. A high-crystallized Co1−xMgxFe2O4 with a cubic structure was obtained when the precursor was calcined at 500°C in air for 2h. The specific saturation magnetizations of Co1−xMgxFe2O4 depend on the calcination temperature and composition. The thermal transformation of the precursor from ambient temperature to 850°C in air presented two steps. The values of the activation energies associated with the thermal transformation of CoC2O4–2FeC2O4·5.77H2O were determined based on the KAS equation.
What problem does this paper attempt to address?