Abstract:Pure and Pr6O11-doped CaCu3Ti4O12 (CCTO) ceramics were prepared by conventional solid-state reaction method. The compositions and structures were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The influences of Pr-ion concentration on dielectric properties of CCTO were measured in the ranges of 60Hz–3MHz and 290–490K. The third phase of Ca2CuO3 was observed from the XRD of CCTO ceramics. From SEM, the grain size was decreased obviously with high valence Pr-ion (mixing valence of Pr3+ and Pr4+) substituting Ca2+. The room temperature dielectric constant of Pr-doped CCTO ceramics, sintered at 1323K, was an order of magnitude lower than the pure CCTO ceramics due to the grain size decreasing and Schottky potential increasing. The dielectric spectra of Pr-doped CCTO were flatter than that of pure CCTO. The loss tangent of Pr-doped CCTO ceramics was less than 0.20 in 2×102–105 Hz region below 440K. The complex impedance spectra of pure and Pr-doped CCTOs were fitted by ZView. From low to high frequency, three semicircles were observed corresponding to three different conducting regions: electrode interface, grain boundary and grain. By fitting the resistors R and capacitors C, the activation energies of grain boundary and electrode contact were calculated. All doped CCTOs showed higher activation energies of grain boundary and electrode than those of pure CCTO ceramics, which were concordant with the decreasing of dielectric constant after Pr6O11 doping.

Dielectric properties of PI hybrid film doped by CaCu3Ti3.95Zr0.05O12 ceramics with different particle sizes

Research Update: Polyimide/CaCu3Ti4O12 Nanofiber Functional Hybrid Films with Improved Dielectric Properties

CaCu33Ti44O1212 Films Prepared by Magnetron S Puttering

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Tailored Wide-Frequency Dielectric Behavior of Polyimide Composite Films with Ba X Sr 1-X TiO 3 Perovskites Ceramic Particles

Improved dielectric strength and loss tangent by interface modification in PI@BCZT/PVDF nano-composite films with high permittivity

Synthesis and properties of PI composite films using carbon quantum dots as fillers

Microstructures and Pyroelectric Properties of Multicomposition 0.9PbZrO<sub>3</sub>·<i>x</i>PbTiO<sub>3</sub>·(0.1−<i>x</i>)Pb(Zn<sub>1/3</sub>Nb<sub>2/3</sub>)O<sub>3</sub>Ceramics

Electrical Properties of TiO2-filled Polyimide Nanocomposite Films Prepared Via an in Situ Polymerization Process

Polyimide/mica hybrid films with low coefficient of thermal expansion and low dielectric constant

Fabrication, Characterization, Properties and Theoretical Analysis of Ceramic/pvdf Composite Flexible Films with High Dielectric Constant and Low Dielectric Loss

Preparation and Characterization of Poled Nanocrystal and Polymer Composite PZT/PC Films

Dielectric Properties of Polyimide/Mesoporous Silica Composite Films

Dielectric Relaxation Behaviors of Pure and Pr6o11-Doped Cacu3ti4o12 Ceramics in High Temperature Range

The Effect of TiO2 on the Dielectric Performance of ZrO2 and Nb2O5 Pre-Doped CaCu3Ti4O12 Ceramics

Process and Microstructure to Achieve Ultra-high Dielectric Constant in Ceramic-Polymer Composites

Dielectric Properties of Pb(Zr20Ti80)O3/Pb(Zr80Ti20)O3 Multilayered Thin Films Prepared by Rf Magnetron Sputtering

Investigation of the Size Effect on the Giant Dielectric Constant of CaCu 3 Ti 4 O 12 Ceramic

Modified poly(phenylene oxide)/(CaSr)TiO 3 composites with ultrahigh permittivity and low loss for microwave substrates

Dielectric, Magnetic, And Magnetoelectric Properties Of Laminated Pbzr0.52ti0.48o3/Cofe2o4 Composite Ceramics