Effect of sintering temperature on the dielectric, impedance and piezoelectric properties of Ba0.85Ca0.15Ti0.90Sn0.09Zr0.01O3 ceramics
Ku Noor Dhaniah Ku Muhsen,Rozana Aina Maulat Osman,Mohd Sobri Idris,Nur Izzati Muhammad Nadzri,Mohammad Hafizuddin Hj Jumali
DOI: https://doi.org/10.1007/s00339-022-05631-9
2022-05-20
Applied Physics A: Materials Science and Processing
Abstract:Ba 0.85 Ca 0.15 Ti 0.90 Sn 0.09 Zr 0.01 O 3 ceramics were prepared by the conventional solid-state route. The effect of different sintering temperatures (1250 °C, 1350 °C, and 1450 °C) on the structural, dielectric, piezoelectric, and microstructure of the samples was investigated. The ceramics exhibited a tetragonal structure with a space group of P4mm and demonstrated a stable crystal structure despite the different sintering temperatures. The ceramic samples obtained similar Curie temperature, T c approximately ~ 60 °C. Among all, the sample sintered at 1450 °C showed an improved pellet's relative density with the highest dielectric constant, ε r value at T c of 6615. The sintering effect gives ~ 53% increment on dielectric constant at T c due to the enhancement of the pellet density from 80.35% (sintered at 1250 °C) up to 91.21% (sintered at 1450 °C). Meanwhile, the sample sintered at 1250 °C obtained the highest piezoelectric constant, d 33 value, due to the small grain size of 5.186 μm, which might lead to more 90° domain wall motion. The equivalent circuit analysis shows that the electrical microstructures of the samples were influenced by their ceramic microstructures. The sample sintered at 1450 °C exhibits an excellent fit using two sets of the parallel resistor, R and capacitor, C ; R 1 – C 1 (grain) and R 2 – C 2 (grain boundary) elements. However, samples sintered at 1350 °C and 1250 °C required a constant phase element (CPE) to fit the R 2 – C 2 element.
materials science, multidisciplinary,physics, applied