Abstract:An unidirectional ultra-high modulus M40J carbon fiber reinforced 5A06 aluminum alloy with volume fraction of 55% was fabricated by the pressure infiltration method. The effect of thermal cycling (−70 to 120°C and −196 to 120°C) on the mechanical properties of Cf/Al composites was investigated. Bending modulus increased abruptly after five thermal cycles and then reached a platform. However, after 50 cycles, the bending modulus decreased with the increase of cycles due to generation and propagation of microcracks at C fiber/Al interface. The bending strength of composites showed fluctuations between 800 and 1000MPa, and the amount and length of pull-out fiber increased with the increase of the thermal cycling times regardless of temperature difference. Microstructure observation revealed the formation of microcracks and interface debonding at the C fiber/Al interface after thermal cycling treatment, and the amount of the microcracks and interface debonding increased with the temperature difference. The main interfacial products in annealed Cf/Al composites were rod-like Al3Mg2 and bulky Al58Mg42, and no significant Al4C3 was observed at C fiber/Al interface. The thermal cycling treatment used in the present work had little effect on the interface microstructure of Cf/Al composites. Very few dislocations were observed in the Al matrix of annealed Cf/Al composites. However, the amount of dislocations in the Al matrix increased gradually with the increase of thermal cycles. Moreover, the amount of dislocations would decrease after a certain thermal cycles due to movement and annihilation of unlike-sign dislocations.

Mechanical Property of M40J F /5a06al Composite at Elevated Temperatures

Effect of thermal cycling on the mechanical properties of Cf/Al composites

Microstructure evolution and tensile behavior of MgAlB4w/Al composites at high temperatures

Effect of TM (tm=fe, Mn, Cr) Alloying on the High Temperature Properties and Strengthening Mechanism of Cf/Al Composites

Mechanical Properties and Microstructures of Steel-basalt Hybrid Fibers Reinforced Cement-based Composites Exposed to High Temperatures

Compressive behavior of high particle content B4C/Al composite at elevated temperature

Experimental Study on Effect of Temperature on Mechanical Properties of Graphite Fibre Reinforced Al Matrix Composites

Interface and Thermal Expansion of Carbon Fiber Reinforced Aluminum Matrix Composites

Improvement of the tensile strength of Al18B4O33w/Al composite at elevated temperatures by change of interfacial state

Hot deformation behavior and microstructural evolution of particulate reinforced AA6061/B4C composite during compression at elevated temperature

Microstructure and Mechanical Properties of Al–B 4 C Composite at Elevated Temperature Strengthened with in Situ Al 2 O 3 Network

The Effect of Thermal Exposure on the Interface and Mechanical Properties of Al(18)B(4)O(33)W/Az91 Magnesium Matrix Composite

Elevated-temperature properties evaluation of Mg-intermetallic laminated composites

Equicohesive Temperature of the Interface and Matrix and Its Effect on the Tensile Plasticity of Al18b4o33 Whiskers Reinforced Aluminum Composite at Elevated Temperatures

Synthesis of an (Al3BC + Al2O3)/Al composite with high stiffness and attractive high-temperature tensile properties

Compressive deformation behavior of α-Si3N 4w/4032 Al composite at elevated temperatures

Ambient and Elevated Temperature Mechanical Properties of Hot-Pressed Fused Silica Matrix Composite

Microstructure Evolution and Mechanical Properties of a Particulate Reinforced Magnesium Matrix Composites Forged at Elevated Temperatures

Effect Of Thermal Exposure On The Microstructure Of The Interface In A Gr(F)/Al Composite

The Role of Al4C3 Morphology in Tensile Properties of Carbon Fiber Reinforced 2024 Aluminum Alloy during Thermal Exposure

High Temperature Mechanical Properties and Wear Performance of B4C/Al7075 Metal Matrix Composites