Abstract:Ti–6Al–4V sheets of 3 mm thickness were joined via friction stir welding (FSW) technique using industrial purpose I-STIR machine. Since the welding speed is a key parameter in production, it was varied from 40 to 200 mm/min in steps of 40 mm/min. Sound joints were obtained without macroscopic defects using a lanthanated tungsten tool. The microstructure, hardness, and residual stress of the joints were evaluated. Stir zone encountered phase transformation and the microstructure of the base metal transformed into a lamellar structure resembling a widmanstätten structure. There was a marginal improvement in hardness subsequent to welding. Tensile kind of residual stresses were recorded along the longitudinal direction of the weld seam. Compressive stresses were observed outside the weld region. Fatigue tests were carried in as welded and polished condition at a stress ratio of 0.1. All specimens failed at the stir zone irrespective of the surface condition and the welding speed. Shoulder formed striation marks served as crack initiation sites for as welded specimens. Slip bands within the lamellar structure or root flaws act as crack initiators in case of polished specimens. The microstructural variation influenced the fatigue strength to a certain degree. The increase in welding speed lowered the fatigue strength.

Microstructural studies of friction stir welded Zircaloy-4

Microstructure evolution and high cycle fatigue failure behavior of friction stir-welded Ti–6Al–4V at varying welding speeds

Microstructural Characteristics and Mechanical Properties of Ti–6Al–4V Friction Stir Welds

Microstructural Evolution and Mechanical Properties of Friction Stir Welded Mg–Zn–Y–Zr Alloy

Effect of Friction Stirring on Microstructure in Equal Channel Angular Pressed Aluminum Alloys

Microstructural Evolution During Friction Stir Welding of Ultrafine Grained Al Alloys

Microstructure and Properties in Friction Stir Weld of 12cr Steel

Microstructure and Mechanical Properties of Friction Stir Lap Welded Dissimilar Zirconium-Steel Joint

The Stir Zone Microstructure and Its Formation Mechanism in Ti–6Al–4V Friction Stir Welds

Microstructural Evolution in 304 Austenitic Stainless Steel During Friction Stir Welding

Microstructural characteristics and effects of TC4 titanium alloy processed by using friction stir welding

Microstructural Analysis of the Stir Zone of Al Alloy Produced by Friction Stir Spot Welding

Microstructure Evolution Of Metallic Materials During Friction Stir Welding

Microstructural Factors Governing Mechanical Properties in Friction Stir Welds

Microstructural Evolution Characterization of Friction Stirring Welded Az31 Magnesium Alloy

Microstructures and Mechanical Properties of Micro Friction Stir Welding (μfsw) of 6061-T4 Aluminum Alloy

Microstructure and Mechanical Properties in Friction Stir Welded 5A06 Aluminum Alloy Thick Plate

Microstructure of Friction Stir Weld for Tc4 Titanium Alloy

Microstructure and mechanical properties of friction stir welded AC4A+30vol.%SiCp composite

Stir Zone Microstructure of Commercial Purity Titanium Friction Stir Welded Using Pcbn Tool

Effect of microstructural evolution on mechanical properties of friction stir welded ZK60 alloy