Microstructural Evolution Characterization of Friction Stirring Welded Az31 Magnesium Alloy

H Zhang,SB Lin,L Wu,JC Feng

IF: 6.318

2004-01-01

Rare Metals

Abstract:A friction stirring welding to joint 5 mm rolled AZ31 magnesium had been developed. The microstructures in various regions including the weld nugget, thermo-mechanically affected zone (TMAZ) and heat affected zone (HAZ) were investigated and compared with unaffected parent metal using optical microscopy. The results showed that the heat and mechanical process had great effect on the microstructure evolution. In weld nugget, the heat was enough to produce sufficient superplastic material flow and the mechanical effect was greatest, and the dynamic recrystallization was completed thoroughly. In TMAZ, the mechanical effect was indirectly affected by the welding tool and only some grains had undergone dynamic recrystallization. The various regions were studied in detail to better understand the microstructural evolution during friction stirring welding (FSW). The cross section near the "key hole" showed clear onion rings because the material was stirred only by the rotation of the probe and materials rotated with the probe and did not move along welding direction and in vertical direction, there was no material flow and the flow movement can be regarded as two dimensional layer flow.