Research on Microstructures and Mechanical Properties in Friction Stir Welded Joints of TC11 Titanium Alloy
Wang Xin,Xie Wenhui,Lou Zhengji,Liu Hong,Yang Guanjun,He Guangyu,Zhou Li
2022-01-01
Rare Metal Materials and Engineering
Abstract:Friction stir welding test of TC11 titanium alloy was carried out under different rotational speeds, the microstructures and mechanical properties of the welded joints were analyzed, and the relationships among processing parameters, microstructures and properties of the joints were established. The results show that the SZ is characterized by beta transformed microstructure, which contains grain boundary alpha phase, intragranular lamellar alpha+beta phases and acicular alpha' phase. The double strengthening is caused by the fine alpha phase and alpha+beta phases as well as the presence of alpha' phase, which leads to the highest hardness value in the SZ. The retained original alpha phase and beta transformed microstructure are found in the HAZ and TMAZ, while the TMAZ shows the streamlined deformation characteristics. The proportion of beta transformed microstructure in these zones is higher when closer to the SZ, and thus the strengthening effect is enhanced. The sizes of alpha phase and alpha+beta phases increase and the content of alpha' phase decreases with the rotational speed ascending, which results in the reduction of hardness value in the SZ. Similar to the law reflected from the hardness test, all the joints fracture in BM after tensile test, the tensile strength of the SZ under different rotational speeds are significantly higher than that of BM, and they decrease with the ascent of rotational speed. Besides, the fine alpha phase and alpha+beta phases cause the higher elongation of SZ compared with that of BM, meaning that the SZ has good plasticity. With the rotational speed ascending, the elongation of SZ decreases owing to the increase of the sizes of alpha phase and alpha+beta phases.