Abstract:A Cu bicrystal with a twin boundary (TB) inclined at 45° to the loading direction and its component monocrystal were specially designed to reveal their fatigue cracking mechanisms. Experimental results show that slip bands (SBs) parallel to the TB plane operated easily in both component grains and concentrated at the TB, while the SBs distributed more homogeneously in the monocrystal. It was revealed by atomistic modeling simulations and anisotropic elasticity theory that the screw dislocations transmitted to the TB could dissociate into two far-separated partial dislocations. Therefore, these dislocations would be confined in the TB with a high difficulty of cross-slip, leading to strain localization near the TB. With cyclic deformation, the fatigue crack nucleated along the TB preferentially in the bicrystal with fewer cycles than that for the SB crack in the monocrystal. Besides, unlike the impingement fatigue crack along high-angle grain boundaries with dislocation impingement, the shear fatigue crack initiates along the TB devoid of dislocation pile-ups. The existence of the TB inclined at 45° to the loading direction induces strain localization and early intergranular fatigue cracking in the Cu bicrystal. These results could not only expand our knowledge of fatigue cracking mechanisms by clarifying how the boundary behaves without the piling up of dislocations, but also provide important implications for future interfacial optimization of materials.

Difference in fatigue cracking behaviors of Cu bicrystals with the same component grains but different twin boundaries

Strain localization and fatigue cracking behaviors of Cu bicrystal with an inclined twin boundary

Interactions Between Dislocations and Penta-Twins in Metallic Nanocrystals

A review on the fatigue cracking of twin boundaries: Crystallographic orientation and stacking fault energy

Effect of grain size on fatigue cracking at twin boundaries in a CoCrFeMnNi high-entropy alloy

Crack bifurcation behavior of coarse-grained copper under cyclic torsion combined with axial static loading

Intersectant Coherent Twin Boundaries Governed Strong Strain Hardening Behavior in Nanocrystalline Cu

Cracking in a Fe–25Mn–3Si–3Al Steel

Twin Boundaries: Strong or Weak?

Atomistic Mechanisms of Fatigue in Nanotwinned Metals

Plastic deformation response during crack propagation in Mg bicrystals with twin boundaries

Effect of Twin Boundary Density on Mechanical Behavior of Al0.1CoCrFeNi High-Entropy Alloy by Molecular Dynamics Simulation

Lattice distortion of a (0001) twin constrained by grain boundaries in a p-type (bi,Sb) 2 Te 3 alloy during three point bending deformation

In situ high-cycle fatigue reveals the importance of grain boundary structure in nanocrystalline Cu-Zr

Interlamellar boundaries govern cracking

Atomistic simulations of twin boundary effect on the crack growth behaviour in BCC Fe

Influence of grain boundary and twin boundary on the stretching deformation behaviors of Cu/Ta interface material

Effects of crystallographic orientations and grain boundaries on nanoscratching behaviour of unique bi-crystal Cu

Deciphering the interactions between single arm dislocation sources and coherent twin boundary in nickel bi-crystal

Quantifying the effect of twin boundaries on grain boundary activities in nanotwinned copper: A molecular dynamics simulation

In Situ Observation of Fracture along Twin Boundaries in Boron Carbide