Achieving superior electrical performance of high-temperature piezoelectric ceramics for high-power applications via MnO2 doping and intentional Ti nonstoichiometry for inhibiting pyrochlore phase
Xuewen Peng,Tianwen Zhu,Ting Wang,Xunzhong Shang,Taosheng Zhou,Weiping Gong,Jinming Guo
DOI: https://doi.org/10.1007/s10853-023-08526-z
IF: 4.5
2023-06-12
Journal of Materials Science
Abstract:Simultaneous achievement of large piezoelectric responses and broad service temperature range for power-type applications, such as sensors, actuators and transducers, is challenging due to trade-off between piezoelectric coefficient ( d 33 ) and Curie temperature ( T C ). In this study, manganese dioxide (MnO 2 ) was introduced in 0.04BiYbO 3 -0.96Pb(Zr 0.469 Ti 0.531 )O 3 (BY-PZT) matrix, and then based on this, Q m further was improved and tan δ got reduced via optimization of Zr/Ti ratios in the matrix, i.e., by intentional design of Ti nonstoichiometry for inhibiting pyrochlore phase. Results show that doping of appropriate amount of MnO 2 led to significant increase in Q m of BY-PZT ceramics from 160 to 274, and tan δ decreased from 2% to 0.3%, while nonstoichiometry with certain Ti-deficiency amount could further increase Q m to 567 and reduce tan δ to 0.2%. Simultaneously, T C was still maintained at relatively high level for high-temperature applications. Ceramics with optimized composition of 0.04BiYbO 3 -0.96Pb(Zr 0.469 Ti 0.531–1.5% )O 3 + 1.3 mol%MnO 2 sintered at 1100 °C exhibited optimal electrical properties of d 33 = 252 pC·N −1 , k p = 0.468, Q m = 567, tan δ = 0.2%, and T C = 389 °C. This study solves the problem of generation of pyrochlore phase during mass production of BY-PZT-based ceramics, and results pave the way for utilizing new power-type piezoelectric ceramic in high-temperature applications.
materials science, multidisciplinary