Low-temperature co-fired PZNN-PZT multilayer piezoelectric ceramics with excellent electrical and bending properties
Jing Zhang,Yaxiong Guo,Qibin Liu,Fangfang Zeng
DOI: https://doi.org/10.1016/j.jsamd.2023.100640
IF: 7.382
2023-10-12
Journal of Science Advanced Materials and Devices
Abstract:A 0.65Pb(Zr 0.47 Ti 0.53 )O 3 –0.35[Pb(Zn 0.1 Ni 0.9 ) 1/3 Nb 2/3 ]O 3 (PZNN-PZT) piezoceramic with sintering aids of Li 2 CO 3 , Bi 2 O 3 , CuO and Sm 2 O 3 was prepared via a traditional solid reaction to achieve a high-performance multilayer actuator. The microstructure and electrical properties of ceramic bulks were systematically explored. The piezoceramics sintered at various temperatures show multi-phase co-existence. The sintering aids are much beneficial for grain growth and microstructure densification. The piezoceramic sintered at 960 o C possesses relatively desirable electrical properties, including d 33 ∼ 550 pC/N, k p ∼ 0.7 ε r ∼ 2200, tan δ ∼ 0.021, Q m ∼71, T c ∼240.5 °C, P r ∼24.44 μC/cm 2 and E c ∼823.7 V/cm. Furthermore, we employed the tape casting and low-temperature co-fire methods to fabricate a PZT-PZNN/Ag-Pd multilayer piezoceramic of 7 × 7 × 36 mm 3 in dimension with a single ceramic film of about 80 μm in thickness. The Ag-Pd electrode is effectively bonded with the ceramic layer, especially chemical binding induced by oxygen diffusion at some partial areas, which plays a crucial role in high binding strength (∼9.2 MPa). The multilayer piezoceramic exhibits outstanding actuating characteristics of high S max ∼ 55.53 μm @ 150V, and low H ∼ 19.8% @ 150V together with outstanding stiffness of 70.87 N/μm @ 150V.
materials science, multidisciplinary,nanoscience & nanotechnology