Abstract:The class of NbC-Ni cermets has emerged as a promising environmentally friendly alternative to WC-Co cemented carbide tools, although some inherent properties i.e. room temperature hardness and flexural strength, of NbC-Ni cermets may require further enhancements. To enhance the properties of NbC-Ni cermets, diverse methodologies were applied, including grain inhibition and the strengthening of the cermet through the use of reinforcements. This study systematically examined the impact of TiC additions, specifically at 10% and 20%, on both the microstructure and mechanical properties of NbC-12Ni-4VC-4Mo2C cermets. NbC-12Ni cermets were fabricated via vacuum liquid phase sintering (LPS) at 1400°C and 1450°C. Enhancements by incorporating 4% VC and 4% Mo2C, followed by TiC at 10% and 20% concentrations to the NbC-Ni-4VC4Mo2C cermet were made. XRD and SEM results confirm the formation of (Nb, X, Y) C solid solution cubic FCC carbides. Significant grain refinement was evident in the cermet samples, subjected to grain inhibition. The observed grain sizes ranged from a maximum of 6.84 μm (in NbC12Ni) to a minimum of 2.154 μm (in the sample containing 20% TiC) at 1450°C. The incorporation of 20TiC at 1450°C led to a remarkable 26.5% enhancement in average hardness compared to NbC-Ni cermet, and a 4.2% improvement over the 4VC4Mo2C cermet. At 1450°C, 20TiC reinforcement led to an average fracture toughness of 9.331 MPa√m, representing a 4.56% improvement over the 4VC4Mo2C cermet. However, there was a marginal reduction in toughness compared to the NbC-Ni cermet. Moreover, the addition of TiC led to a decrease in the flexural strength of the cermets, with a maximum flexural strength of 939 N/mm2 recorded for NbC-Ni-4VC4Mo2C, representing an 11.6% increase compared to the NbC-Ni cermet.

Thermal shock behavior of co-continuous TiCx-Cu cermets in air and anaerobic environment

Thermal Shock Performance of CVD Tungsten Coating at Elevated Temperatures

Influence of Surface Morphology and Microstructure on Performance of CVD Tungsten Coating under Fusion Transient Thermal Loads

Effect of WC Content on Thermal Shock Resistance of Ti(C,N)-based Cermets

Study on the Behavior in Thermal Shock and Ablation Resistance of TiC-TiB2/Cu Ceramic-Matrix Composite

Influence of Thermal Shock on the Mechanical Behavior of Si-SiC Coated Carbon/Carbon Composites

Thermal Shock Resistance and Ablation Behaviour of Titanium Diboride-Copper-Nickle Fgm Via Shs

Research On Wear Behavior Of Atc Cermet Material

Thermal shock behavior of Ti2AlC from 200 °C to 1400 °C

Repeated Thermal Shock Behavior of the ZrB2–SiC–ZrC Ultrahigh-Temperature Ceramic

High-temperature Ablation Behavior of TiB2-Cu Matrix Cermets

Insights into Hardening and Strengthening in Ultrafine Ti(C, N)-Based Cermets

Microstructure and Mechanical Properties of TiC Reinforced NbC-Ni4VC4Mo2C Cermets

Thermal Shock Behavior of a Novel TiCx–Ni3(Al,Ti)/Ni Functionally Graded Composite

Influence of TaC content on microstructure and mechanical performance of Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Mechanical and Physical Properties of Cu2O−xCu Cermet

Evolution of microstructure and interfacial characteristics of complete solid-solution Ti(C,N)-based cermets fabricated by mechanical activation and subsequent in situ carbothermal reduction

Tuning microstructure for superb mechanical properties in a Ti(C,N)-(WMoTaNbTi)C-Ni/Co cermets via change sintering temperature

Strengthening and toughening of Ti(C,N)-based cermets: (Ti,W)C additive design and the mechanism

Microstructure and thermal shock behavior of ZrB2–SiC–graphite composite

Fabrication, microstructure evolution, and mechanical properties of Ti(C,N)-HfN-WC-Ni-Mo cermets