Abstract:Semiconducting single-walled nanotube (s-SWNT) arrays with specific diameters are urgently demanded in the applications in nanoelectronic devices. Herein, we reported that by using uniform Mo2C solid catalyst, aligned s-SWNT (similar to 90%) arrays with narrow-diameter distribution (similar to 85% between 1.0 and 1.3 nm) on quartz substrate can be obtained. Mo2C nanoparticles with monodisperse sizes were prepared by using molybdenum oxide-based giant clusters, (NH4)(42)[Mo132O372(H3CCOO)(30)(H2O)(72)]. 10H(3)CCOONH(4)center dot 300H(2)O(Mo-132), as the precursor that was carburized by a gas mixture of C2H5OH/H-2 during a temperature-programmed reduction. In this approach, the formation of volatile MoO3 was inhibited due to the annealing and reduction at a low temperature. As a result, uniform Mo2C nanoparticles are formed, and their narrow size-dispersion strictly determines the diameter distribution of SWNTs. During the growth process, Mo2C selectively catalyzes the scission of C-O bonds of ethanol molecules, and the resultant absorbed oxygen (O-ads) preferentially etches metallic SWNTs (m-SWNTs), leading to the high-yield of s-SWNTs. Raman spectroscopic analysis showed that most of the s-SWNTs can be identified as (14, 4), (13, 6), or (10, 9) tubes. Our findings open up the possibility of the chirality-controlled growth of aligned-SWNTs using uniform carbide nanoparticles as solid catalysts for practical nanoelectronics applications.

Selective Scission of C-O and C-C Bonds in Ethanol Using Bimetal Catalysts for the Preferential Growth of Semiconducting SWNT Arrays.

Water-Assisted Preparation of High-Purity Semiconducting (14,4) Carbon Nanotubes

Selective growth of semiconducting single-walled carbon nanotubes solely from carbon monoxide

Selective Synthesis Combined with Chemical Separation of Single-Walled Carbon Nanotubes for Chirality Selection

Diameter-Specific Growth Of Semiconducting Swnt Arrays Using Uniform Mo2c Solid Catalyst

Bimetallic Catalysts for the Efficient Growth of SWNTs on Surfaces

Growth of close-packed semiconducting single-walled carbon nanotube arrays using oxygen-deficient TiO2 nanoparticles as catalysts

Selective Growth Of Chirality-Enriched Semiconducting Carbon Nanotubes By Using Bimetallic Catalysts From Salt Precursors

How Catalysts Affect the Growth of Single-Walled Carbon Nanotubes on Substrates

Growth of Horizontal Semiconducting SWNT Arrays with Density Higher Than 100 Tubes/μm Using Ethanol/Methane Chemical Vapor Deposition

Importance of diameter control on selective synthesis of semiconducting single-walled carbon nanotubes.

Growth and Characterization of Bamboo-Like Multiwalled Carbon Nanotubes over Cu/Al2o3 Catalyst

Solid supported ruthenium catalyst for growing single-walled carbon nanotubes with narrow chirality distribution

Growth of semiconducting single-walled carbon nanotubes by using ceria as catalyst supports.

Selective Growth of Metal‐Free Metallic and Semiconducting Single‐Wall Carbon Nanotubes

Superlong-oriented Single-Walled Carbon Nanotube Arrays on Substrate with Low Percentage of Metallic Structure

Sorting out Semiconducting Single-Walled Carbon Nanotube Arrays by Preferential Destruction of Metallic Tubes Using Water

Confined Fe Catalysts for High‐Density SWNT Arrays Growth: a New Territory for Catalyst‐Substrate Interaction Engineering

Designing Catalysts for Chirality-Selective Synthesis of Single-Walled Carbon Nanotubes: Past Success and Future Opportunity

Metal-catalyst-free growth of single-walled carbon nanotubes.

Atomic Layer Deposition of Al2O3 Catalysts for Narrow Diameter Distributed Single-Walled Carbon Nanotube Arrays Growth