Epigallocatechin-3-gallate Enhance Dentin Biomodification and Bond Stability of an Etch-and-rinse Adhesive System
Qiurong Sun,Lisha Gu,Jingjing Quan,Xiaoran Yu,Zihua Huang,Ruoxun Wang,Sui Mai
DOI: https://doi.org/10.1016/j.ijadhadh.2017.11.001
IF: 3.848
2018-01-01
International Journal of Adhesion and Adhesives
Abstract:Objectives: To evaluate the effect of epigallocatechin gallate (EGCG) on hydrophobicity, thermal stability of dentin collagen, and the influence of EGCG preconditioning on resin-dentin bonds. Methods: Coronal dentin specimens were sectioned to 0.7 mm or 2.5 mm from the dental pulp horn to simulate deep and shallow dentin. Static contact angle measurements on 0.005%, 0.02%, 0.1%, 0.5%EGCG preconditioned demineralized dentin were performed by contact angle analyzer. The collagen thermal denaturation temperature was determined by differential scanning calorimetry (DSC) analysis. Resin-bonded specimens with/without EGCG preconditioning as well as thermocycling were created for microtensile bond strength evaluation. Confocal laser microscopy (CLSM) was used to evaluate the ultra-morphology and micropermeability of the resin-dentin interface after thermocycling. Results: Contact angle of demineralized dentin substrate increased after 0.02%/0.1%/0.5%EGCG preconditioning. Statistical analysis revealed that the effect of EGCG on shallow dentin was more evident than on deep dentin. The results of DSC demonstrated that 0.1%/0.5%EGCG strengthened collagen's resistance to thermal denaturing. 0.1%EGCG preconditioning group showed highest bond strength after thennocyling aging and exhibited least nanoleakage under CLSM examination. 0.5%EGCG preconditioning resulted in thinner hybrid layers. Meanwhile, bonding interface presented more nanoleakage in 0.5%EGCG group than in 0.1% EGCG preconditioning group. Conclusions: 0.1%EGCG preconditioning improved the hydrophobicity of dentin substrate and thermal stability of dentin collagen, which could reduce nanoleakage and enhance resin-dentin bond durability.