Abstract:Nanocomposite particles of amorphous carbon-Li4Ti5O12 (C-LTO) and carbon nanotube-Li4Ti5O12 (CNT-LTO) were synthesized by solvothermal method and subsequent high-temperature calcination. X-ray diffraction (XRD), transmission electron microscopy (TEM), high-resolution transmission electron microscopy (HR-TEM), and selected area electron diffraction (SAED) were applied to characterize the phase structure, particle morphology, and the coating structure. XRD analysis, TEM micrographs, HR-TEM images and SAED analysis revealed that both LTO particles exhibited a well- developed spinel nanocrystal structure with average sizes between 20-70 nm. The C-LTO particles exhibited roughly spherical shape coated by an amorphous carbon layer up to 10 nm in thickness. The CNT-LTO samples showed uniform square nanocrystals with edge length around 20 nm and nanoscale graphitic layers covering the surface, revealing the carbon nanotubes interconnection networks among the particle assemblies. Electrochemical studies of lithium insertion/extraction performance are evaluated by the galvanostatic charge/discharge tests, cyclic voltammetry (CV) and electrochemical impedance spectroscopy (EIS). Both LTO particles showed the superior initial discharge capacity of more than 200 mAh/g at 1/10C rate. The irreversible capacity of the C-LTO particles at more cycles was due to large polarization resulted from excessive carbon and possible residual precursors. The CNT-LTO particles show larger reversible capacity and enhanced electrochemical Li+ insertion/extraction kinetics at different cycling rates. The comparative structural and electrochemical analyses demonstrated that both nanoscale graphitic covering layers and the CNT interconnection networks increase the electronic conductivity and improve the kinetics rates of lithium insertion/extraction in the CNT-LTO particles.

Fast solution-combustion synthesis of nitrogen-modified Li4Ti5O12 nanomaterials with improved electrochemical performance.

Nitrogen and sulfur co-doped carbon-coated Li4Ti5O12 composite to enhance lithium storage properties

Structure and Electrochemical Properties of Spinel Li4ti5o12 Nanocomposites As Anode for Lithium-Ion Battery

Nanocomposites As Anode for Lithium-Ion Battery

Synthesis and electrochemical performance of nanoporous Li4Ti5O12 anode material for lithium-ion batteries

Confined Growth of Li4ti5o12 Nanoparticles in Nitrogen-Doped Mesoporous Graphene Fibers for High-Performance Lithium-Ion Battery Anodes

Structural Analysis and Electrochemical Studies of Carbon Coated Li4ti5o12 Particles Used As Anode for Lithium Ion Battery

Highly Crystalline Lithium Titanium Oxide Sheets Coated with Nitrogen-Doped Carbon Enable High-Rate Lithium-Ion Batteries.

Enhancing Ultrafast Lithium Ion Storage of Li4Ti5O12 by Tailored TiC/C Core/Shell Skeleton Plus Nitrogen Doping

Effect of Carbon Nanotubes Addition on Electrochemical Performance and Thermal Stability of Li4Ti5O12 Anode in Commercial Li Mn2O4/Li4Ti5O12 Full-Cell

Synthesis and Electrochemical Performance of Li4Ti5O12 Submicrospheres Coated with TiN As Anode Materials for Lithium-Ion Battery

Improved electrochemical performance of nitrogen doped TiO2-B nanowires as anode materials for Li-ion batteries

Scalable in Situ Synthesis of Li4Ti5O12/Carbon Nanohybrid with Supersmall Li4Ti5O12 Nanoparticles Homogeneously Embedded in Carbon Matrix

Preparation of Carbon Nanotube Coated Li4Ti5O12 Nanosheets Heterostructure As Ultrastable Anodes for Lithium-Ion Batteries

Electrochemical performance of Li 4 Ti 5 O 12 /carbon nanofibers composite prepared by an in situ route for Li-ion batteries

Nitrogen-sodium co-doping improves cycle performance of lithium titanate anode materials at high rate

Improved Electrochemical Properties of Li 4 Ti 5 O 12 Nanopowders (NPs) via Addition of LiAlO 2 and Li 6 SiON Polymer Electrolytes, Derived from Agricultural Waste

Synthesis of Li4Ti5O12 Nanostructural Anode Materials with High Charge–discharge Capability

Titania and Nitrogen-Doped Carbon Co-Modification: Their Synergic Effects on the Electrochemical Performance of LiFePO4

Li4Ti5O12 Nanoparticles Prepared with Gel‐hydrothermal Process As a High Performance Anode Material for Li‐ion Batteries

Synthesis and assessment of the electrochemical performance of micro-nano-spherical Li4Ti5O12-LiAlO2 composites