Microstructured Sulfur-Doped Carbon-Coated Fe 7 S 8 Composite for High-Performance Lithium and Sodium Storage
Feng Jiang,Limin Zhang,Wenqing Zhao,Jiahui Zhou,Peng Ge,Li Wang,Yue Yang,Wei Sun,Xinghua Chang,Xiaobo Ji
DOI: https://doi.org/10.1021/acssuschemeng.0c03936
2020-07-17
Abstract:From the perspective of resource reserves, environmental effects, and production costs, direct utilization of natural ores as electrode materials for rechargeable batteries after mineral processing is of more practical significance than chemosynthetic materials. While the corresponding investigation is relatively insufficient, herein phenolic resin (PR)-coated natural pyrite composite (FeS<sub>2</sub>@PR) is successfully fabricated using natural pyrite and oligomeric phenolic resin as starting materials. Subsequent oligomer polymerization and calcination process convert FeS<sub>2</sub>@C into sulfur-doped carbon-coated Fe<sub>7</sub>S<sub>8</sub> (). Benefiting from the good electric and ionic conductivity of Fe<sub>7</sub>S<sub>8</sub>, abundant sulfur active sites, and porosity on carbon shell and effective carbon buffering, exhibits impressive electrochemical performance as anodes for lithium-ion batteries (LIBs) and sodium-ion batteries (SIBs). It delivers high reversible capacities of 1319 and 796 mAh g<sup>–1</sup> after 100 cycles at 0.1 A g<sup>–1</sup> for LIBs and SIBs, respectively. Even at a high current density of 2.0 A g<sup>–1</sup>, considerable capacities of 771 mAh g<sup>–1</sup> after 1000 cycles and 545 mAh g<sup>–1</sup> after 400 cycles are retained for LIBs and SIBs. This work provides a promising prospect toward scalable production of high-capacity iron sulfide anode for lithium-ion and sodium-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c03936?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c03936</a>.Preparation scheme of Fe<sub>7</sub>S<sub>8</sub>@C; Raman, TGA, and XPS analyses of samples; element mapping of ; CV curves and charge/discharge curves of and pristine pyrite; SEM, TEM, and HRTEM images of the electrode after long cycles; Nyquist plots of the pyrite electrode; <i>R</i><sub>ct</sub> values of , , and pyrite electrodes; and comparison of our work with previous Fe<sub>7</sub>S<sub>8</sub>-based materials (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c03936/suppl_file/sc0c03936_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.
chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology