ChemInform Abstract: A Potential Pyrrhotite (fe7s8) Anode Material for Lithium Storage.

Kailong Zhang,Tingwei Zhang,Jianwen Liang,Yongchun Zhu,Ning Lin,Yitai Qian

DOI: https://doi.org/10.1002/chin.201520017

2015-01-01

ChemInform

Abstract:AbstractFe7S8@C nanospheres with diameters of 30—40 nm are synthesized by solid state reaction of ferrocene and (NH4)2S2O8 (autoclave, 230 °C, 1 h) followed by calcination at 500 °C for 2 h in a flow of Ar.

What problem does this paper attempt to address?

Microstructured Sulfur-Doped Carbon-Coated Fe 7 S 8 Composite for High-Performance Lithium and Sodium Storage

Feng Jiang,Limin Zhang,Wenqing Zhao,Jiahui Zhou,Peng Ge,Li Wang,Yue Yang,Wei Sun,Xinghua Chang,Xiaobo Ji

DOI: https://doi.org/10.1021/acssuschemeng.0c03936

2020-07-17

Abstract:From the perspective of resource reserves, environmental effects, and production costs, direct utilization of natural ores as electrode materials for rechargeable batteries after mineral processing is of more practical significance than chemosynthetic materials. While the corresponding investigation is relatively insufficient, herein phenolic resin (PR)-coated natural pyrite composite (FeS2@PR) is successfully fabricated using natural pyrite and oligomeric phenolic resin as starting materials. Subsequent oligomer polymerization and calcination process convert FeS2@C into sulfur-doped carbon-coated Fe7S8 (). Benefiting from the good electric and ionic conductivity of Fe7S8, abundant sulfur active sites, and porosity on carbon shell and effective carbon buffering, exhibits impressive electrochemical performance as anodes for lithium-ion batteries (LIBs) and sodium-ion batteries (SIBs). It delivers high reversible capacities of 1319 and 796 mAh g–1 after 100 cycles at 0.1 A g–1 for LIBs and SIBs, respectively. Even at a high current density of 2.0 A g–1, considerable capacities of 771 mAh g–1 after 1000 cycles and 545 mAh g–1 after 400 cycles are retained for LIBs and SIBs. This work provides a promising prospect toward scalable production of high-capacity iron sulfide anode for lithium-ion and sodium-ion batteries.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acssuschemeng.0c03936?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acssuschemeng.0c03936</a>.Preparation scheme of Fe7S8@C; Raman, TGA, and XPS analyses of samples; element mapping of ; CV curves and charge/discharge curves of and pristine pyrite; SEM, TEM, and HRTEM images of the electrode after long cycles; Nyquist plots of the pyrite electrode; Rct values of , , and pyrite electrodes; and comparison of our work with previous Fe7S8-based materials (<a class="ext-link" href="/doi/suppl/10.1021/acssuschemeng.0c03936/suppl_file/sc0c03936_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

chemistry, multidisciplinary,engineering, chemical,green & sustainable science & technology
Hollow Structured Carbon@FeSe Nanocomposite As a Promising Anode Material for Li‐Ion Batteries

Yu Chen,Jie Shao,Xiaoyu Lin,Yuanyuan Gu,Rudolf Holze,Yuanxing Yun,Qunting Qu,Honghe Zheng

DOI: https://doi.org/10.1002/celc.201801722

IF: 4

2018-01-01

ChemElectroChem

Abstract:Carbon@FeSe nanocomposites with homogeneous hollow microspherical and nanotubular structures are prepared using sulfonated polystyrene microspheres and sulfonated poly(divinylbenzene) nanotubes as both the template and carbon source. Benefiting from their hollow core-shell and hierarchical micro/nanostructures, the carbon@FeSe nanocomposites as the anode material of Li-ion batteries exhibit high capacities with a steady discharge plateau of 1.5 V (vs. Li/Li+), stable cycling performance (700 mAhg(-1) in the 200th cycle at 800 mAg(-1)), and good rate behavior (620 mAhg(-1) at 16 Ag-1). The steady discharge plateau of carbon@FeSe, together with its high capacity, renders it a promising anode material for Li-ion batteries.
Fe3O4/C Composites Synthesized from Fe-based Xerogels for Anode Materials of Li-ion Batteries

Xiao Yan Chen,Bin Hong Liu,Zhou Peng Li

DOI: https://doi.org/10.1016/j.ssi.2014.04.004

IF: 3.699

2014-01-01

Solid State Ionics

Abstract:In this study, Fe3O4/carbon nanocomposites as anode materials of Li-ion batteries were synthesized through heating hierarchically porous Fe-based xerogels under N2 atmosphere. The pyrolysis of amorphous Fe-xerogel base materials resulted in the simultaneous formation of Fe3O4/C composites, in which Fe3O4 particles of less than 50nm were uniformly dispersed and embedded in a porous carbon matrix. Due to the favorable nanostructure, the synthesized Fe3O4/C composites with a proper carbon content of 18.8wt.% exhibited good electrochemical performance including high capacity and rate capability as well as much enhanced cyclic stability.
In-situ synthesis of Fe7S8 nanocrystals decorated on N, S-codoped carbon nanotubes as anode material for high-performance lithium-ion batteries

Xiaojie Zhang,Xiaoyan Gao,Junfeng Li,Kun Hong,Lei Wu,Shigang Xu,Kailong Zhang,Chenzhen Liu,Zhonghao Rao

DOI: https://doi.org/10.1016/j.jcis.2020.06.087

IF: 9.9

2020-11-01

Journal of Colloid and Interface Science

Abstract:Fe7S8 has emerged as an attractive anode material for lithium-ion batteries (LIBs) due to its outstanding features such as low cost, high theoretical capacity, as well as environmental benignity. However, the rapid capacity fading derived from the tremendous volume change during the charging/discharging process hinders its practical application. Nanostructure engineering and the combination with carbonaceous material are essential to address this issue. In this work, Fe7S8 nanocrystals decorated on N, S-codoped carbon nanotubes (Fe7S8-NSC) were synthesized through a facile one-step pyrolysis of Fe-containing polypyrrole (PPy) nanotubes with sulphur powders under nitrogen atmosphere. When evaluated as anode of LIBs, Fe7S8-NSC demonstrates excellent cycling stability (718.8 mAh g-1 at 100 mA g-1 after 100 cycles) and superior rate ability (290.8 mAh g-1 at 2000 mA g-1). Moreover, Fe7S8-NSC shows a typical specific capacity recovery phenomenon, an extraordinary capacity of 744.4 mAh g-1 at 2000 mA g-1 after 1000 cycles can be achieved, which outperforms most of the Fe7S8-based anode materials reported before. The Fe7S8-NSC should be a promising anode material for high-performance LIBs.

chemistry, physical
Fes2 Microsphere As Cathode Material for Rechargeable Lithium Batteries

Yiming Tao,Kun Rui,Zhaoyin Wen,Qingsong Wang,Jun Jin,Tao Zhang,Tian Wu

DOI: https://doi.org/10.1016/j.ssi.2016.04.005

IF: 3.699

2016-01-01

Solid State Ionics

Abstract:The spherical pyrite FeS2 was synthesized through a green and simple method with the addition of the polyvinylpyrrolidone (PVP) dispersant. The as-prepared FeS2 displays a good electrochemical performance with an initial specific capacity over 80% of the theoretical value and a very low decay rate of 0.33% per cycle (calculated from 2nd to 50th at 0.1C). Rate capability testing exhibits discharge capacities of around 371.6mAh/g (0.1C), 343mAh/g (0.2C), 294.9mAh/g (0.5C), 239mAh/g (1C) and 161.8mAh/g (2C) respectively. Besides, coulombic efficiency close to 100% at various rates can also be obtained. We calculate Li+ diffusion coefficient and multi-electron feature of the pyrite FeS2 during charge/discharge process. It shows that smaller potential window is beneficial for cyclability, which was in good agreement with experimental results.
Hydrothermal Synthesis of FeS 2 for Lithium Batteries

Xu Feng,Xiangming He,Weihua Pu,Changyin Jiang,Chunrong Wan

DOI: https://doi.org/10.1007/s11581-007-0136-5

IF: 2.961

2007-01-01

Ionics

Abstract:Nanocrystalline FeS2 cathode material of lithium cell was synthesized from cheap materials of FeSO4, Na2S2O3, and sulfur by a hydrothermal process. The scanning electron microscopy analysis showed the obtained material was nano-sized, about 500 nm. The X-ray powder diffraction analysis showed that the synthetic FeS2 material had two phases of the crystalline structure, pyrite and marcasite. The phase of marcasite seems to have no negative effect on the electrochemical performance of the material. The synthetic FeS2 showed a significant improvement of electrochemical performance for Li/FeS2 cells.
One-Step Route to Fe2O3 and FeSe2 Nanoparticles Loaded on Carbon-Sheet for Lithium Storage

Denghu Wei,Leilei Xu,Zhiqi Wang,Xiaojie Jiang,Xiaxia Liu,Yuxue Ma,Jie Wang

DOI: https://doi.org/10.3390/molecules27092875

IF: 4.6

2022-04-30

Molecules

Abstract:Iron-based anode materials, such as Fe2O3 and FeSe2 have attracted widespread attention for lithium-ion batteries due to their high capacities. However, the capacity decays seriously because of poor conductivity and severe volume expansion. Designing nanostructures combined with carbon are effective means to improve cycling stability. In this work, ultra-small Fe2O3 nanoparticles loaded on a carbon framework were synthesized through a one-step thermal decomposition of the commercial C15H21FeO6 [Iron (III) acetylacetonate], which could be served as the source of Fe, O, and C. As an anode material, the Fe2O3@C anode delivers a specific capacity of 747.8 mAh g-1 after 200 cycles at 200 mA g-1 and 577.8 mAh g-1 after 365 cycles at 500 mA g-1. When selenium powder was introduced into the reaction system, the FeSe2 nano-rods encapsulated in the carbon shell were obtained, which also displayed a relatively good performance in lithium storage capacity (852 mAh g-1 after 150 cycles under the current density of 100 mA·g-1). This study may provide an alternative way to prepare other carbon-composited metal compounds, such as FeNx@C, FePx@C, and FeSx@C, and found their applications in the field of electrochemistry.
Fe3O4 Submicron Spheroids As Anode Materials for Lithium-Ion Batteries with Stable and High Electrochemical Performance

Suqing Wang,Jingying Zhang,Chunhua Chen

DOI: https://doi.org/10.1016/j.jpowsour.2010.03.035

IF: 9.2

2010-01-01

Journal of Power Sources

Abstract:A magnetite (Fe3O4) powder composed of uniform sub-micrometer spherical particles has been successfully synthesized by a hydrothermal method at low temperature. X-ray diffraction, scanning electron microscopy, transmission electron microscopy and galvanostatic cell cycling are employed to characterize the structure and electrochemical performance of the as-prepared Fe3O4 spheroids. The magnetite shows a stable and reversible capacity of over 900mAhg−1 during up to 60 cycles and good rate capability. The experimental results suggest that the Fe3O4 synthesized by this method is a promising anode material for high energy-density lithium-ion batteries.
One-Step Route to Fe2O3 and FeSe2 Nanoparticles Loaded on Carbon-Sheet for Lithium Storage

Denghu Wei,Leilei Xu,Zhiqi Wang,Xiaojie Jiang,Xiaxia Liu,Yuxue Ma,Jie Wang

DOI: https://doi.org/10.3390/molecules27092875

2022-01-01

Abstract:Iron-based anode materials, such as Fe2O3 and FeSe2 have attracted widespread attention for lithium-ion batteries due to their high capacities. However, the capacity decays seriously because of poor conductivity and severe volume expansion. Designing nanostructures combined with carbon are effective means to improve cycling stability. In this work, ultra-small Fe2O3 nanoparticles loaded on a carbon framework were synthesized through a one-step thermal decomposition of the commercial C15H21FeO6 [Iron (III) acetylacetonate], which could be served as the source of Fe, O, and C. As an anode material, the Fe2O3@C anode delivers a specific capacity of 747.8 mAh g(-1) after 200 cycles at 200 mA g(-1) and 577.8 mAh g(-1) after 365 cycles at 500 mA g(-1). When selenium powder was introduced into the reaction system, the FeSe2 nano-rods encapsulated in the carbon shell were obtained, which also displayed a relatively good performance in lithium storage capacity (852 mAh g(-1) after 150 cycles under the current density of 100 mA center dot g(-1)). This study may provide an alternative way to prepare other carbon-composited metal compounds, such as FeNx@C, FePx@C, and FeSx@C, and found their applications in the field of electrochemistry.
Preparation of a Sulfur-Doped Graphene-Wrapped FeS 2 Microsphere Composite Material for Lithium-Ion Batteries

Yating Zhang,Zhanrui Zhang,Yongling Zhang,Peng Wang,Pengfei Han,Keke Li,Wei Liu

DOI: https://doi.org/10.1021/acs.energyfuels.1c02999

2021-11-30

Abstract:Pyrite (FeS2) is considered a promising anode material for lithium-ion batteries (LIBs) relying on its high theoretical specific capacity and low cost. However, the application of FeS2 as anodes has been greatly limited due to its low electrical conductivity and huge volume expansion during cycling. In this work, a facile approach was developed to prepare an FeS2 and sulfur-doped graphene (SG) composite (FeS2/SG). The product exhibits good electrochemical performance in terms of a high capacity of 1033.4 mAh·g–1 at 0.1 A·g–1 after 60 cycles and good rate performance because of its conductive network and porous structure. Therefore, the FeS2/SG composite can be considered a candidate material for LIB anodes considering such desirable electrochemical performances and the economic synthesis route.

energy & fuels,engineering, chemical
Nanosized Fe7S8 with High Surface Area As Polysulfide Capturer Combined with Graphene for Li–S Battery Cathode

Hang Zhang,Qiuming Gao,Xuehui Tian,Zeyu Li,Peng Xu,Hong Xiao

DOI: https://doi.org/10.1016/j.electacta.2019.07.023

IF: 6.6

2019-01-01

Electrochimica Acta

Abstract:Lithium-sulfur (Li-S) battery system shows immense potential as energy storage devices with high energy density. However, the soluble property of polysulfides into the electrolyte during charge/discharge process leads to low sulfur utilization, severe polarization and short cyclic life, which has been a serious obstacle for practical application. How to anchor the polysulfides onto the cathode materials and moreover, enhance its further conversion to the final products, have been important challenges for the utilization of Li-S batteries. Herein, a novel well crystallized nanosized Fe7S8 possessing of a high specific surface area of 55.6 m(2) g(-1) fabricated by a simple microwave-assisted method combined with high temperature pyrolysis technique, is introduced into the S/C composite cathode for the first time. Strong interaction between polysulfides and the Fe7S8 can be realized to relieve the shuttle effect. The redox reaction of polysulfides can also be promoted to reduce electrode polarization. As a result of the enhanced utilization of sulfur, the optimized S@GFS-15 electrode may deliver a high initial discharge capacity of 1307.2 mA h g(-1) at 0.1 C (1 C = 1675 mA h g(-1)) and low decay rates of 0.047% and 0.037% per cycle after 1000 cycles at 1 and 2 C respectively when the sulfur loading is ordinary 1.1 mg cm(-2). Even the sulfur loading rises up to 2.6 mg cm(-2), a large initial discharge specific capacity of 1134.5 mA h g(-1) can be achieved at 0.1 C. After 600 cycles, the specific capacity of 457.3 mA h g(-1) with a relatively small average decay rate of 0.062% per cycle can be obtained. Thus, incorporation of the nanosized Fe7S8 with graphene can help to achieve effective performance improvement route for Li-S batteries. (C) 2019 Elsevier Ltd. All rights reserved.
High Lithium Storage Performance of Fes Nanodots in Porous Graphitic Carbon Nanowires

Changbao Zhu,Yuren Wen,Peter A. van Aken,Joachim Maier,Yan Yu

DOI: https://doi.org/10.1002/adfm.201404468

IF: 19

2015-01-01

Advanced Functional Materials

Abstract:Much attention has been paid to increase the energy density of Li‐ion batteries, in order to fulfill the requirements of electric vehicles and grid‐scale energy storage. While for anodes various options are available, this is not at all the case for cathodes. In this context, the inexpensive and environmentally benign iron sulfides have been investigated as cathode materials due to the remarkably high capacity based on the conversion reaction. Here, the preparation of FeS nanodots accommodated in porous graphitic carbon nanowires is reported via a combination of electrospinning technique and biomolecular‐assisted hydrothermal method. These materials exhibit excellent electrochemical performances also as cathode materials, with energy densities even higher than the current LiCoO2 intercalation cathode. Moreover, key problems of conversion reaction, such as the low degree of reversibility, large polarization are far‐reachingly mitigated.
FeS Nanosheets As Positive Electrodes for All-Solid-state Lithium Batteries

Qiang Zhang,Xiayin Yao,Jean Pierre Mwizerwa,Ning Huang,Hongli Wan,Zhen Huang,Xiaoxiong Xu

DOI: https://doi.org/10.1016/j.ssi.2017.09.007

IF: 3.699

2018-01-01

Solid State Ionics

Abstract:Transition metal sulfides have attracted particular interests owing to their extremely higher specific capacity and more compatible with sulfide electrolyte than lithium transition-metal oxide for all-solid-state lithium batteries. FeS nanosheets with thickness of 10nm are synthesized by a poly (vinyl alcohol)-assisted precipitation method and further successfully employed in Li/70%Li2S-29%P2S5–1%P2O5/Li10GeP2S12/FeS all-solid-state lithium batteries. The obtained all-solid-state lithium batteries show reversible discharge capacity of 550mAhg−1 after 50cycles at current density of 0.1Ag−1 and exhibit superior rate performances.
ChemInform Abstract: Decoration of Sulfur with Porous Metal Nanostructures: an Alternative Strategy for Improving the Cyclability of Sulfur Cathode Materials for Advanced Lithium—Sulfur Batteries.

Xinyong Tao,Feng Chen,Yang Xia,Hui Huang,Yongping Gan,Xiaorong Chen,Wenkui Zhang

DOI: https://doi.org/10.1002/chin.201331011

2013-01-01

ChemInform

Abstract:Pt@S nanostructures are prepared from mixtures of pristine sulfur microparticles (obtained from aqueous mixtures of sodium polysulfide, ZnCl2, and H2O2), aqueous H2PtCl6, and NaBH4 solutions.
Carbon‐Encapsulated Pyrite As Stable and Earth‐Abundant High Energy Cathode Material for Rechargeable Lithium Batteries

Jun Liu,Yuren Wen,Yi Wang,Peter A. van Aken,Joachim Maier,Yan Yu

DOI: https://doi.org/10.1002/adma.201401496

2014-01-01

Advances in Materials

Abstract:Cathode materials consisting of porous pyrite nano-octahedra encapsulated by uniform carbon nanocages exhibit very high energy density, superior rate capability (reversible capabilities of 439, 340, and 256 mA h g(-1) at 1C, 2.5C, and 5C, respectively) and stable cycling performance (ca. 10% capacity loss after 50 cycles at 0.5C with a capacity retention of 495 mA h g(-1) ).
ChemInform Abstract: an Fe3O4—FeO—Fe@C Composite and Its Applications As Anode for Lithium‐Ion Battery.

Xiuyun Zhao,Dingguo Xia,Kun Zheng

DOI: https://doi.org/10.1002/chin.201209009

2012-01-01

ChemInform

Abstract:The title composite material is hydrothermally synthesized from a 5:1 mixture of FeSO4 and glucose in H2O (autoclave, 180 °C, 9 h) followed by heating the obtained precursor at 700 °C for 1 h under a nitrogen atmosphere.
Controlling Electrochemical Lithiation/Delithiation Reaction Paths for Long-cycle Life Nanochain-structured FeS2 Electrodes

Jie Yang,Meinan Liu,Zhanhua Wei,Zhenghui Pan,Yongcai Qiu,Fangmin Ye,Yali Yang,Xinluo Zhao,Leimei Sheng,Yuegang Zhang

DOI: https://doi.org/10.1016/j.electacta.2016.06.067

IF: 6.6

2016-01-01

Electrochimica Acta

Abstract:Pyrite (FeS2) stands out from other metal sulfides due to its abundance, low toxicity and high specific energy density. However, the low utilization and short cycle life of FeS2 caused by irreversible side reactions and dramatic structural changes during charge/discharge process seriously hinders its practical application. In this work, we designed FeS2 nanochains to address these issues because this unique structure not only shortens the ion/electron diffusion distance, increases the electrode/electrolyte contact area, but also accommodates the strain associated with Li ion intercalation and deintercalation reactions. Compared with nanoparticles, the FeS2 nanochains synthesized by magnetic-field-assisted aerosol pyrolysis could cycle up to 800 cycles at 0.5C, remained a discharge capacity of 342.4mAhg−1 in the voltage range of 1.0-2.6V and achieved a remarkable capacity fading rate of 0.02% per cycle, which is among the best values demonstrated so far for Li/FeS2 cells. In-situ Raman experiments revealed that the irreversible side reactions could be suppressed through controlling the voltage window, which can be benefit for further improving the performance of Li/FeS2 cells.
Electrochemical Properties of CoFe 3 Sb 12 As Potential Anode Material for Lithium-Ion Batteries

Zhao Xin-bing,Zhong Yao-dong,Cao Gao-shao

DOI: https://doi.org/10.1631/jzus.2004.0418

2004-01-01

Journal of Zhejiang University SCIENCE A

Abstract:A skutterudite-related antimonide, CoFe3Sb12, was prepared with vacuum melting. XRD analysis showed the material contained Sb, FeSb2, CoSb2 and CoSb3 phases. The electrochemical properties of the ball-milled CoFe3Sb12-10 wt% graphite composite were studied using pure lithium as the reference electrode. A maximal lithium inserting capacity of about 860 mAh/g was obtained in the first cycle. The reversible capacity of the material was about 560 mAh/g in the first cycle and decreased to ca. 320 mAh/g and 250 mAh/g after 10 and 20 cycles respectively. Ex-situ XRD analyses showed that the antimonides in the pristine material were decomposed after the first discharge and that antimony was the active element for lithium to insert into the host material.
Homogeneous Distributed Natural Pyrite-Derived Composite Induced by Modi-Fied Graphite As High-Performance Lithium-Ion Batteries Anode

Juan Yu,Yinbo Wei,Bicheng Meng,Jiaxin Peng,Kai Yang,Tianxing Chen,Naixing Yang,Xiuyun Chuan

DOI: https://doi.org/10.1007/s12613-023-2598-5

2023-01-01

Abstract:Natural minerals-based energy materials have attracted enormous attention because of the advantages of good materials consistency, high production, environmental friendliness, and low cost. The uniform distribution of grains can effectively inhibit the aggregation of active materials, improving lithium storage performance. In this work, natural graphite is modified by polyvinylpyrrolidone to obtain modified graphite with reduced size and better dispersion. Natural pyrite composite polyvinylpyrrolidone-modified graphite (pyrite/PG) material with uniform particle distribution is obtained by the ball milling process. The subsequent calcination process converts pyrite/PG into Fe1−xS compounded with polyvinylpyrrolidone-modified graphite (Fe1−xS/PG). The homogeneous grain distributions of active material can facilitate the faster transfer of electrons and promote the efficient utilization of active materials. The as-prepared Fe1−xS/PG electrode exhibits a remarkably reversible specific capacity of 613.0 mAh·g−1 at 0.2 A·g−1 after 80 cycles and an excellent rate capability of 523.0 mAh·g−1 at 5 A·g−1. Even at a higher current density of 10 A·g−1, it can deliver a specific capacity of 348.0 mAh·g−1. Moreover, the dominant pseudocapacitance in redox reactions accounts for the impressive rate and cycling stability. This work provides a low-cost and facile method to fabricate natural mineral-based anode materials and apprise readers about the impact of uniform particle distribution on lithium storage performance.
Confining Pyrrhotite Fe 7 S 8 in Carbon Nanotubes Covalently Bonded onto 3D Few‐Layer Graphene Boosts Potassium‐Ion Storage and Full‐Cell Applications

Kun Han,Fuqiang An,Qi Wan,Lidong Xing,Lei Wang,Qiang Liu,Wei Wang,Yongchang Liu,Ping Li,Xuanhui Qu,Wei (Alex) Wang

DOI: https://doi.org/10.1002/smll.202006719

IF: 13.3

2021-03-01

Small

Abstract:The pyrrhotite Fe7S8 with mixed Fe‐valence possesses high theoretical capacity, high conductivity, low discharge/charge voltage plateaus, and superior redox reversibility but suffers from structural degradation upon (de)potassiation process due to severe volume variations. Herein, to conquer this issue, a novel hierarchical architecture of confining nano‐Fe7S8 in carbon nanotubes covalently bonded onto 3D few‐layer graphene (Fe7S8@CNT@3DFG) is designed for potassium storage. Notably, CNTs could successfully grow on the surface of 3DFG via a tip‐growth model under the catalytic effect of Fe3C. Such structure enables the hierarchical confinement of 0D nano‐Fe7S8 to 1D CNTs and further 1D CNTs to 3DFG, effectively buffering the volume variations, prohibiting the agglomeration of Fe7S8 nanograins, and boosting the ionic/electronic transportation through the stable and conductive CNTs‐grafted 3DFG framework. The as‐prepared Fe7S8@CNT@3DFG electrode delivers an exceptional rate capability (502 mAh g−1 at 50 mA g−1 with 277 mAh g−1 at 1000 mA g−1) and an excellent long‐term cyclic stability up to 1300 cycles. Besides, the in‐situ XRD and ex‐situ XPS/HRTEM results first elucidate the highly reversible potassium‐storage mechanism of Fe7S8. Furthermore, the designed potassium full‐cell employing Fe7S8@CNT@3DFG anode and potassium Prussian blue (KPB) cathode delivers a promising energy density of ≈120 Wh kg−1, demonstrating great application prospects.

materials science, multidisciplinary,chemistry, physical,physics, applied, condensed matter,nanoscience & nanotechnology

ChemInform Abstract: A Potential Pyrrhotite (fe7s8) Anode Material for Lithium Storage.

Microstructured Sulfur-Doped Carbon-Coated Fe 7 S 8 Composite for High-Performance Lithium and Sodium Storage

Hollow Structured Carbon@FeSe Nanocomposite As a Promising Anode Material for Li‐Ion Batteries

Fe3O4/C Composites Synthesized from Fe-based Xerogels for Anode Materials of Li-ion Batteries

In-situ synthesis of Fe7S8 nanocrystals decorated on N, S-codoped carbon nanotubes as anode material for high-performance lithium-ion batteries

Fes2 Microsphere As Cathode Material for Rechargeable Lithium Batteries

Hydrothermal Synthesis of FeS 2 for Lithium Batteries

One-Step Route to Fe2O3 and FeSe2 Nanoparticles Loaded on Carbon-Sheet for Lithium Storage

Fe3O4 Submicron Spheroids As Anode Materials for Lithium-Ion Batteries with Stable and High Electrochemical Performance

One-Step Route to Fe<sub>2</sub>O<sub>3</sub> and FeSe<sub>2</sub> Nanoparticles Loaded on Carbon-Sheet for Lithium Storage

Preparation of a Sulfur-Doped Graphene-Wrapped FeS 2 Microsphere Composite Material for Lithium-Ion Batteries

Nanosized Fe7S8 with High Surface Area As Polysulfide Capturer Combined with Graphene for Li–S Battery Cathode

High Lithium Storage Performance of Fes Nanodots in Porous Graphitic Carbon Nanowires

FeS Nanosheets As Positive Electrodes for All-Solid-state Lithium Batteries

ChemInform Abstract: Decoration of Sulfur with Porous Metal Nanostructures: an Alternative Strategy for Improving the Cyclability of Sulfur Cathode Materials for Advanced Lithium—Sulfur Batteries.

Carbon‐Encapsulated Pyrite As Stable and Earth‐Abundant High Energy Cathode Material for Rechargeable Lithium Batteries

ChemInform Abstract: an Fe3O4—FeO—Fe@C Composite and Its Applications As Anode for Lithium‐Ion Battery.

Controlling Electrochemical Lithiation/Delithiation Reaction Paths for Long-cycle Life Nanochain-structured FeS2 Electrodes

Electrochemical Properties of CoFe 3 Sb 12 As Potential Anode Material for Lithium-Ion Batteries

Homogeneous Distributed Natural Pyrite-Derived Composite Induced by Modi-Fied Graphite As High-Performance Lithium-Ion Batteries Anode

Confining Pyrrhotite Fe 7 S 8 in Carbon Nanotubes Covalently Bonded onto 3D Few‐Layer Graphene Boosts Potassium‐Ion Storage and Full‐Cell Applications