Influence of Cyclic Loading on the Fracture Toughness and Load Bearing Capacities of All-Ceramic Crowns

Rao-Rao Wang,Cheng-Lin Lu,Gang Wang,Dong-Sheng Zhang

DOI: https://doi.org/10.1038/ijos.2013.94

2014-01-01

Abstract:The purpose of this study was to investigate how cyclic loading influenced the fracture toughness of hot-press lithium disilicate and zirconia core materials and whether there was an increase in the propensity for crown failure. Two types of all-ceramic crowns including the IPS e.max Press system ( n =24) and the Lava zirconia system ( n =24), were selected. Sectioned specimens were subjected to cyclic loading with the maximum magnitude of 200 N ( R =0.1) until two million cycles. The material properties including Young's modulus ( E ) and hardness ( H ) and the fracture toughness ( K IC ) of the core materials were evaluated using indentation methods ( n =12 each). The load-bearing capacities of the specimens were examined by means of monotonic load to fracture ( n =12 each). It was found that the material properties, including E , H and K IC , of the two types of dental ceramics, were reduced. Statistical analysis indicated that there were no significant influences of fatigue loading on material properties E and H for both types of dental ceramics or K IC for zirconia, while for the IPS e.max Press core, K IC , which was parallel to the direction of the lithium disilicate crystals, was significantly reduced ( P =0.001). A conclusion was drawn that zirconia possesses high mechanical reliability and sustainable capacity to resist fatigue loading, while fatigue loading remarkably degraded the anisotropic mechanical behaviour of hot-press lithium disilicate ceramics.