Abstract:It is well known that the mechanical properties of spheroidal graphite cast iron deeply depend on the volume of pearlite matrix microstructures. Therefore, the theoretical criterion of pearlite matrix nucleation is considered important in this graphite cast iron that to obtain the higher mechanical properties of graphite cast iron, the pearlite stabilizing element such as Mn or Cu is very important. The present work aims to study the influence of manganese (Mn) content and heat treatment on the mechanical properties of 3% or 4% (Solution Strengthened Ferritic Ductile Iron-SSFDI) of silicon (Si) containing spheroidal graphite cast irons. The six 3.6%C–3%Si melts with different chemical compositions from 0.2 to 1.7 mass% of Mn content were produced using a high-frequency induction furnace. The melt was poured into a Y-block CO 2 sand mold of 25 or 40 mm in thickness. The microstructure analysis and mechanical testing were performed for as-cast and some heat treatment conditions, such as annealing or air cooling. As a result, the tensile strength had a good relationship with the area fraction of pearlite, over 600 MPa in UTS, and high proof stress for some 3 or 4%Si–Mn series samples in the as-cast condition. By the heat treatment from the unique ( α + γ ) region, the 3% Si sample showed over 800 MPa and over 10% in elongation. And 4%Si–1.5%Mn (SSFDI) series sample showed over 600 MPa in UTS and over 15% in elongation which was prepared by annealing heat treatment to reduce to less than 5% of the area fraction of pearlite. This study suggests that it can be understood of the correlation between optimizing the heat treatment condition and mechanical properties of SSFDI cast irons.

Determination of Silicon, Manganese and Magnesium in Cast Iron by Atomic Emission Spectrometry

Application of improved EMD-Elman neural network to predict silicon content in hot metal

Determination of Cr, Ni, Cu, Mn, P, Si, Mo and Ti in high chromium cast iron by inductively coupled plasma atomic emission spectrometry

Determination of manganese, iron, cobalt and nickel in air and water by atomic absorption spectroscopy

Simultaneous direct determination of aluminum, calcium and iron in silicon carbide and silicon nitride powders by slurry-sampling graphite furnace AAS

Determination of 13 Components in Slag by X-ray Fluorescence Spectrometry

Determination of fourteen elements in iron oxide by microwave digestion inductively coupled plasma atomic emission spectrometry

Determination of Microamount of Silicon in Steel by Inductively Coupled Plasma-Atomic Emission Spectrometry

Experimental Study of a Representative Sample to Determine the Chemical Composition of Cast Iron

[Determination of Fe, Al, Ca, Ti, P and Cu in Silicon Metal by XRF].

Determination of manganese in biological materials by electrothermal atomic absorption spectrometry: a review.

Preparation of an Electrochemical Sensor for Measuring the Silicon Content in Molten Iron

Determination of eight components in converter slag by X-ray fluorescence spectrometry

Comparative analysis of methods for the determination of chromium, vanadium, copper, nickel, and manganese in steel and cast iron by flame atomic absorption spectrometry

Investigation of Selective Oxidation During Cooling of Hot-Rolled Iron-Manganese-silicon Alloys

Emission Characterization of Particulate Matter in the Ironmaking Process

Determination of Trace Elements in Some Seasonings by Microwave Digestion-high Resolution Continuum Source Graphite Furnace Atomic Absorption Spectrophotometry

Effects of Manganese and Heat Treatment on Mechanical Properties in Spheroidal Graphite Cast Iron

ICP-AES Determination of 5 Chemical Components in Chromium Ores

Simultaneous determination of 5 elements in chrome iron ore samples by inductively coupled plasma-opti-cal emission spectrometry

Sequential and Rapid Determination of Metallic Elements in Monosodium Glutamate by Continuum Source Flame Atomic Absorption Spectrophotometry