Abstract:Developing effective carbon materials for post-combustion CO(2)capture (PCC) has received great attentions over many recent years, owing to their desirable adsorption-desorption performance and exceptional thermo-oxidative stability compared to virtually any other capture materials typically the wide array of amine-based sorbent materials. However, due to the nature of physical adsorption, virtually none of the carbon materials reported so far can be practically used for PCC applications without deep flue gas cooling to ambient or even lower temperatures in order to achieve appreciable levels of CO(2)uptake capacities at low CO(2)partial pressures. Here, we present a category of 3D hierarchical molecular sieving carbon architectures that are able to operate at realistic flue gas temperatures with exceedingly high reversible CO(2)capacities. The breakthrough CO2-sieving carbon materials are prepared from using a cost-effective and commercially widely available precursor of polymeric polyisocyanurates with a facile one-step compaction-activation methodology. Tested at sensible flue gas temperatures of 40-70 degrees C and a low CO(2)partial pressure of 0.15 bar, the best performing materials are found to have exceedingly high reversible CO(2)capacities of up to 2.30 mmol g(-1)at 40 degrees C and 1.90 mmol g(-1)at 70 degrees C. Advanced characterisations suggest that the unique geometry and chemistry of the easily available precursor material coupled with the characteristics of the compaction-activation protocol used are responsible for the CO2-sieving structures and capacities of the 3D carbon architectures. The findings essentially change the general perception that carbon-based materials can hardly find applications in post-combustion capture due to their low CO(2)uptake capacity at low CO(2)partial pressures and realistic flue gas temperatures.

Efficient MgO-based Mesoporous CO2 Trapper and Its Performance at High Temperature.

Combined CO2-philicity and Ordered Mesoporosity for Highly Selective CO2 Capture at High Temperatures

Regenerable MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure: Experimental and DFT Study

Synthesis of a Porous Nano‐CaO/MgO‐Based CO2 Adsorbent

Promotion of MgO Sorbents with Eutectic Carbonate Doping for High-Temperature and Pressure CO2 Capture

Characteristics of MgO-based Sorbents for CO2 Capture at Elevated Temperature and Pressure

Design and development of 3D hierarchical ultra-microporous CO2-sieving carbon architectures for potential flow-through CO2 capture at typical practical flue gas temperatures

Fabrication Of A New Mgo/C Sorbent For Co2 Capture At Elevated Temperature

Acquiring an Efficient Warm‐CO2 Sorbent from Advanced Pyrolysis of Magnesium Oxalate

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica as Binder for Low-Temperature CO 2 Capture

MgO-Based Granular Sorbent Pelletized by Using Ordered Mesoporous Silica As Binder for Low-Temperature CO2 Capture

Efficient MgO-doped CaO sorbent pellets for high temperature CO2 capture

Ultrafast and Stable CO 2 Capture Using Alkali Metal Salt-Promoted MgO-CaCO 3 Sorbents.

Facile Synthesis of MOF-5-derived Porous Carbon with Adjustable Pore Size for CO2 Capture

High-temperature CO 2 adsorption on Li XZr YO Z ceramics

Fabrication of Strong Solid Base FeO–MgO for Warm CO2 Capture

Hierarchical porous AlOOH hollow microspheres for efficient CO2 capture

Mesoporous Carbon Stabilized MgO Nanoparticles Synthesized by Pyrolysis of MgCl2 Preloaded Waste Biomass for Highly Efficient CO2 Capture.

A Novel Porous Mgo Sorbent Fabricated Through Carbon Insertion

Synthesis and Performance of a Nano Synthetic Ca-based Sorbent for High Temperature CO_2 Capture

Core‐shell structured CaO‐based pellets protected by mesoporous ceramics shells for high‐temperature CO2 capture