Abstract:Laboratory sliding sphere tests simulate essential features of occlusal contact.At P = 200 N, strength degradation in 3Y- and 5Y-PSZ occurs after <50 sliding cycles.At P = 50 N, strength degradation in both zirconias occurs after 750–1000 sliding.After the first falloff, further occlusal loading only moderately lowers the strength.A 50-N occlusal load can debase the strength of zirconia as much as a 200-N load.Mechanical damages can occur from dental restoration processing and fitting, or while it is in-service. This study evaluates the damage sensitivity of translucent zirconia (5Y-PSZ) relative to conventional 3Y-PSZ following mouth-motion simulations at various loads.5Y-PSZ and 3Y-PSZ discs were adhesively bonded to a dentin-like substrate and divided into groups according to the load (50 N or 200 N) and number of cycles (up to 106) used in the chewing simulation. Specimens were mounted with 30° inclination in an electrodynamic mouth-motion simulator, and subjected to contact-slide-liftoff cyclic loading in water. Surface and sub-surface damages were analyzed using a sectioning technique. After the simulation, specimens were removed from the substrate and loaded with the damaged surface in tension for biaxial strength testing to assess their damage tolerance.The strength of both ceramics underwent significant degradation after mouth-motion simulations. For 5Y-PSZ, the strength degradation was greater (∼60%) and occurred at a lower number of cycles than 3Y-PSZ. Herringbone cracks emerged on 3Y-PSZ and 5Y-PSZ surfaces under a 200-N load after 50 and 10 cycles, respectively. Meanwhile at a 50-N load, cracks formed at ∼1000 cycles in both ceramics. Further increasing the number of cycles only had moderate effects on the strength of both ceramics, despite an increase in surface and sub-surface damage. More significantly, a 50-N occlusal load can debase the zirconia strengths as much as a 200-N load.Surface flaws produced during the chewing simulation are capable of significant strength degradation in zirconia, even after a small number of low-load cycles.<ol class="links-for-figure"><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S0109564120302967-fx1_lrg.jpg">Download : Download high-res image (98KB)</a></li><li><a class="anchor download-link u-font-sans" href="https://ars.els-cdn.com/content/image/1-s2.0-S0109564120302967-fx1.jpg">Download : Download full-size image</a></li></ol>

Sliding Contact Fatigue of Graded Zirconia with External Esthetic Glass

On the interfacial fracture of porcelain/zirconia and graded zirconia dental structures

Using glass-graded zirconia to increase delamination growth resistance in porcelain/zirconia dental structures

Sliding contact wear and subsurface damage of CAD/CAM materials against zirconia

The effect of graded glass-zirconia structure on the bond between core and veneer in layered zirconia restorations

Silica infiltration on translucent zirconia restorations: Effects on the antagonist wear and survivability

Fatigue and failure mode analyses of glass infiltrated 5Y-PSZ bonded onto dentin analogues

Double veneering, low-temperature porcelain, and total glaze application methods to overcome failures of zirconia-based restorations

Extended glaze firings for porcelain-veneered zirconia: Effects on the mechanical and optical behavior

Investigation of the structure and mechanical properties of a novel dental graded glass/zirconia ceramic

Fatigue Behaviours of the Zirconia Dental Restorations Prepared by Two Manufacturing Methods

Self-glazed Zirconia Reducing the Wear to Tooth Enamel

Influence of different surface finishing procedures of strength-gradient multilayered zirconia crowns on two-body wear and fracture load: Lithium silicate or leucite glazing versus polishing?

Effect of low-temperature degradation on the fatigue performance of dental strength-gradient multilayered zirconia restorations

Dynamic wear characteristics and fracture strength of high-translucent monolithic zirconia crowns

Lifetime-limiting strength degradation from contact fatigue in dental ceramics

Monolithic Zirconia Partial Coverage Restorations: An In Vitro Mastication Simulation Study

Effects of Small-Grit Grinding and Glazing on Mechanical Behaviors and Ageing Resistance of a Super-Translucent Dental Zirconia.

Damage sensitivity of dental zirconias to simulated occlusal contact

Two-body Wear Performance of Dental Colored Zirconia after Different Surface Treatments.

Enamel wear against monolithic zirconia restorations: A meta-analysis and systematic review of in vitro studies