Abstract:Objective This study aimed to compare the four-point flexural strength of CAM-milled and sintered (as-sintered, AS) specimens with those of high-polished (HP) specimens using chairside polishing systems to simulate clinical surface conditions. Methods Seven full-contour zirconia CAM/CAM blanks with various yttria contents (3, 4, 5 mol%) including three high-translucent groups (5Y) were selected to prepare flexural specimens. The bend bar specimens (2.0 × 4.0 × 25.0 mm 3 ) were fabricated by using STL file and dental CAM machine with the respective zirconia blanks (98 mm φ and 10–14 mm in height). Twelve bar specimens were machined from one zirconia puck and a total of 24 specimens were prepared from each group. The pre-sintered bar specimens were sintered by using a dental zirconia furnace at 1530–1550 °C for 2 h according to the instructions. All sintered specimens were divided into two groups: as-sintered (AS) group and high-polished (HP) groups (n = 12). HP groups were subjected to polishing one surface of specimens using a three-step polishing system and finally finished with diamond polishing. After cleaning and drying, the flexural strength of all specimens was determined by a fully articulating four-point flexure fixture consisting of a 1/4-point test configuration with an inner/outer span of 10/20 mm. Statistical differences between AS and HP groups were conducted with Weibull analysis. The fractured surfaces of zirconia specimens were observed using a field emission SEM and EDS to detect failure origins. Results The mean AS flexural strength values were significantly lower than those of HP counterparts. However, Weibull moduli expressing the reliability of HP groups were generally decreased although not significantly in comparison to their AS. The fracture of the AS specimens mostly originated from extrinsic CAM-milling defects, while the HP specimens were fractured from intrinsic subsurface or volume defects including pores, large grain clusters, inclusions, and corner-located critical flaws. Two high-translucent (5Y) zirconia groups were not affected in their strength and reliability after polishing, whereas one 5Y zirconia significantly increased its strength but significantly lowered its reliability. Significance The extrinsic and intrinsic strength-limiting defects should be considered in evaluating the flexural strength and reliability of dental CAD/CAM zirconia ceramics for full-contour restorations. For the materials tested in this study, more optimized processing of blanks and milling protocols of pre-sintered zirconia blanks should be developed including post-sintering surface finishing to reduce the flaw population regulating strength and reliability which will affect the survivability of dental zirconia prostheses. Graphical Download : Download high-res image (203KB) Download : Download full-size image

Damage sensitivity of dental zirconias to simulated occlusal contact

Sliding contact wear and subsurface damage of CAD/CAM materials against zirconia

Lifetime-limiting strength degradation from contact fatigue in dental ceramics

Strength-limiting damage and its mitigation in CAD-CAM zirconia-reinforced lithium-silicate ceramics machined in a fully crystallized state

Wear behavior and microstructural characterization of translucent multilayer zirconia

Strength-limiting damage and defects of dental CAD/CAM full-contour zirconia ceramics

Silica infiltration on translucent zirconia restorations: Effects on the antagonist wear and survivability

Monolithic Zirconia Partial Coverage Restorations: An In Vitro Mastication Simulation Study

Impact of sandblasting on the flexural strength of highly translucent zirconia

Dynamic wear characteristics and fracture strength of high-translucent monolithic zirconia crowns

The effects of artificial aging on high translucent zirconia

Impact of the sintering parameters on the grain size, crystal phases, translucency, biaxial flexural strength, and fracture load of zirconia materials

Effect of the CAD/CAM Milling Protocol on the Fracture Behavior of Zirconia Monolithic Crowns

High-versus low-viscosity resin cements: Its effect on the load-bearing capacity under fatigue of a translucent zirconia

Effect of Surface Treatment and Cement on Fracture Load of Traditional Zirconia (3Y), Translucent Zirconia (5Y), and Lithium Disilicate Crowns

Effect of low-temperature degradation on the fatigue performance of dental strength-gradient multilayered zirconia restorations

Fracture behaviour of zirconia ceramic cantilever fixed dental prostheses in vitro

Effect of different CAD/CAM cutting depths on the post-fatigue load-bearing capacity of novel multilayer zirconia restorations

Influence of different surface finishing procedures of strength-gradient multilayered zirconia crowns on two-body wear and fracture load: Lithium silicate or leucite glazing versus polishing?

The Surface Deterioration of Prefabricated Zirconia Crowns on Exposure to Acidulated Phosphate Fluoride Gel: An In Vitro Study

On the interfacial fracture of porcelain/zirconia and graded zirconia dental structures