Magnetostrictions of Sm Fe and Sm Fe N

Yang, J.B.,Chen, H.Y.,Zhang, Y.,Yang, Y.B.

DOI: https://doi.org/10.1109/tmag.2011.2154312

2011-01-01

Abstract:The magnetostrictions of Sm2Fe17N3 and Sm2Fe17 were investigated using strain gauge rotating-sample methods. In a magnetic field of 8 T, the magnetostriction λt (λxt = λ// - λ⊥) of Sm2Fe17 is about -155 × 10-6 at 300 K. It becomes positive after nitrogenation [Sm2Fe17N3, λt is about + 44 × 10-6 at 300 K (H = 8 T)] due to the crystal field effect and the exchange striction. It was noticed that inverse magnetostriction effect can be used to increase the magnetic alignment and remanence of the bonded magnets. As a result, transverse die-pressing (H ⊥P) was very effective in increasing the degree of magnetic alignment of Sm2Fe17N3 powders, yielding remanence higher than that obtained by axial die-pressing (H//P). By increasing the degree of magnetic alignment of powders, the maximum energy product (BH)max of Sm2Fe17N3 bonded magnet was improved by 15%.