Abstract:In this work, the effects of Nb2O5 addition on the dielectric properties and phase formation of BaTiO3 were investigated. A core–shell structure was formed for Nb-doped BaTiO3 resulted from a low diffusivity of Nb5+ ions into BaTiO3 when grain growth was inhibited. In the case of 0.3–4.8 mol% Nb2O5 additions, two dielectric constant peaks were observed. The Curie dielectric peak was determined by the ferroelectric-paraelectric transition of grain core, whereas the secondary broad peak at lower temperature was due to strong chemical inhomogeneity in Nb-doped BaTiO3 ceramics. The dielectric constant peak at Curie temperature was markedly depressed with the addition of Nb2O5. On the other hand, the secondary dielectric constant peak was enhanced when sintered above 1280 °C for higher Nb2O5 concentrations (≥1.2 mol%). The Curie temperature was shifted to higher temperatures, whereas the transition temperature corresponding to the secondary peak moved to lower temperatures as increasing the amount of Nb2O5 more than 1.2 mol%. The decrease of this lower transition temperature was assumed to be closely related with the secondary phase formation when Nb concentration greater than 1.2 mol%. From XRD analyses, a large amount of secondary phases was observed when Nb2O5 amount exceeded 1.2 mol%. The coefficients of thermal expansion of Nb-doped BaTiO3 were increased with increasing Nb2O5 contents, resulting in large internal stress between cores and shells. Therefore, the shift of Curie temperature to higher temperatures was attributed to internal stress resulting from the formation of a core–shell structure and a large amount of secondary phase grains.

Impedance Analysis of Nb2O5 Doped BaTiO3-Na0.5Bi0.5TiO3 Ceramics

Impedance analysis of Nb<inf>2</inf>O<inf>5</inf> doped BaTiO<inf>3</inf>-Na<inf>0.5</inf>Bi<inf>0.5</inf>TiO<inf>3</inf> ceramics

Nb-doped 0.9 BaTiO 3-0.1(Bi 0.5Na 0.5) TiO 3ceramics with stable dielectric properties at high temperature

Nb-Doped 0 . 8 BaTiO 3-0 . 2 Bi ( Mg 0 . 5 Ti 0 . 5 ) O 3 Ceramics with Stable Dielectric Properties at High Temperature

Dielectric behaviors of Nb2O5–Co2O3 doped BaTiO3–Bi(Mg1/2Ti1/2)O3 ceramics

Effect of Na0.5Bi0.5TiO3 on Dielectric Properties of BaTiO3 Based Ceramics

Colossal Dielectric Permittivity in (al+nb) Co-Doped Ba0.4Sr0.6TiO3 Ceramics

Investigation of the modulation effects of BiNbO4 doping on BaTiO3-based ceramics

Effects of Nb 2 O 5 Doping on the Microstructure and the Dielectric Temperature Characteristics of Barium Titanate Ceramics

Doping Behaviors of Nb2O5 and Co2O3 in Temperature Stable BaTiO3-based Ceramics

Effects of BiNbO<sub>4</sub> on the microstructure and dielectric properties of BaTiO<sub>3</sub>-based ceramics

Nb-doped BaTiO3-(Bi0.5Na0.5)TiO3ceramics with Core-Shell Structure for High-Temperature Dielectric Applications

High-temperature Impedance Spectroscopy of BaFe 0.5 Nb 0.5 O 3 Ceramics Doped with Bi 0.5 Na 0.5 TiO 3

Microstructure and Dielectric Characteristics of Nb2O5 Doped BaTiO3-Bi(Znl/2Til/2)O3 Ceramics for Capacitor Applications

Investigation on dielectric properties of BaTiO3 co-doped with Ni and Nb

Dielectric Properties of Batio3-Nb2o5-Ni2o3 Ternary System

Effects of Binbo4 and Nb2O5 additions on the temperature stability of modified BaTiO3

Effects of BiNbO 4 on the microstructure and dielectric properties of BaTiO 3 -based ceramics

Dielectric Relaxation and Maxwell-Wagner Interface Polarization in Nb2O5 Doped 0.65bifeo3–0.35batio3 Ceramics

Effect of MnO2 on the Dielectric Properties of Nb‐doped BaTiO3‐(Bi0.5Na0.5)TiO3 Ceramics for X9R MLCC Applications

Synthesis and Characterization of BaTiO3-(Bi0.5Na0.5)TiO3 Solid Solution Based Dielectric Ceramics