Effects of BiNbO 4 on the microstructure and dielectric properties of BaTiO 3 -based ceramics

Ying Yuan,Min Du,Shuren Zhang,Zhenlin Pei

DOI: https://doi.org/10.1007/s10854-008-9674-5

2008-01-01

Abstract:The microstructure and dielectric properties of ternary system BaTiO 3 (BT)–Bi 0.5 Na 0.5 TiO 3 (BNT)–BiNbO 4 were investigated. In the case of 1 mol% BNT addition, the Curie point ( T c ) of BaTiO 3 was increased from 130 to 140 °C. The dielectric constant peak at T c was markedly depressed with the addition of BiNbO 4 , whereas an enhancement in the dielectric constant at lower temperature was observed. The addition of BiNbO 4 improved the temperature dependence of the dielectric constants of BaTiO 3 -BNT system ceramics and the temperature coefficient of capacitance curves satisfied the EIA X8R specification with 3–4 mol% BiNbO 4 . The dielectric constant peak at T c was suppressed evidently due to over high-sintering temperature. As the BiNbO 4 content was increased, the Curie point progressively moved to lower temperatures. SEM indicated that fine and homogeneous grains were observed with 1 mol% BiNbO 4 addition. However, secondary phase grains appeared with increasing the BiNbO 4 content, which were identified as Ba 2 TiO 4 , NaBiTi 2 O 6 , and BaTiNb 4 O 13 by XRD. Moreover, the proportion of the secondary phase grains increased as the BiNbO 4 content increased.