Abstract:Undoped, Cu and/or Y doped ZrO 2 nanopowders were synthesized with Zr, Y, and Cu nitrates using a co-precipitation approach. Their structural and optical properties were examined regarding dopant content (0.1-8.0 mol.% of CuO and 3-15 mol.% of Y 2 O 3 ) and calcination conditions (400-1000 °C and, 1, 2 or 5 hours) through Raman scattering, XRD, TEM, EDS, AES, ESR, UV-Vis and FTIR diffused reflectance methods. The results showed that both Cu and Y dopants promoted the appearance of additional oxygen vacancies in ZrO 2 host, while the formation of tetragonal and cubic ZrO 2 phases was primarily influenced by the Y content, regardless of Cu loading. The bandgap of the most powders was observed within the 5.45-5.65 eV spectral range, while for those with high Y content it exceeded 5.8 eV. The (Cu,Y)-ZrO 2 powders with 0.2 mol.% CuO and 3 mol.% Y 2 O 3 calcined at 600°C for 2 hours demonstrated nanoscaled tetragonal grains (8-12 nm) and a significant surface area covered with dispersed CuxO species. For higher calcination temperatures, the formation of Cu Zr 2+ ESR centers, accompanied by tetragonal-to-monoclinic phase transformation. For fitting experimental FTIR reflection spectra, theoretical models with one, five, and seven oscillators were constructed for cubic, tetragonal, and monoclinic ZrO 2 phases, respectively. Compared experimental and theoretical spectra, the parameters of various phonons were determined. It was found that the distinct position of the high-frequency FTIR reflection minimum is a unique feature for each crystalline phase. It centered at 700-720 cm -1 , 790-800 cm -1 , and 820-840 cm -1 for cubic, tetragonal, and monoclinic phases, respectively, showing minimal dependence on phonon damping coefficients. Based on the complementary nature of results obtained from structural and optical methods, an approach for monitoring powder properties and predicting catalytic activity can be proposed for ZrO 2 –based nanopowders.

Precursor method for the synthesis of highly dispersed ZrO 2 doped with scandium

Synthesis of Scandia-Stabilized Zirconia Via Thermo-Decomposition of Precursor Complexes

Co-Doping Effects of Y3+ and Sc3+ on the Crystal Structures, Nanoparticle Properties and Electrical Behavior of Zro2 Solid Solutions Prepared by A Mild Urea-Based Hydrothermal Method

One-step combustion synthesis of undoped c-ZrO2 for Cr(VI) removal from aqueous solutions

Hydrothermal Growth of Scandium-Doped ZnO Crystals

Nanocrystalline Cubic Phase Scandium-Stabilized Zirconia Thin Films

Synthesis of PbZrO3 Powder by a COprecipitation Method

Microstructure and synthesis mechanism of ScYSZ powders prepared by chemical co-precipitation with different dynamic microenvironment

Preparation and Thermochromic Properties of Sol-Gel-derived Zr-doped VO 2 Films

Insight of precursor concentration, particle size and band gap of zirconia nanoparticles synthesized by co-precipitation method

Highly efficiently selective separation of zirconium from scandium by TRPO modified adsorbent

Homogeneous Precipitation Synthesis and Electrical Properties of Scandia Stabilized Zirconia

Effect of dopant loading and calcination conditions on structural and optical properties of ZrO2 nanopowders doped with copper and yttrium

Ethanol-induced formation of precursor for 8mol% Yttria-stabilized zirconia: Towards the production of well-dispersed, easily sintering, and high-conductivity nano-powders

Effects of Synthetic Parameters in Pechini Method on the Formation and Properties of (zro2)0.92(sc2o3)0.08 Solid Solution

Sol–gel Synthesis and Electrical Properties of (zro2)0.85(reo1.5)0.15 (RE = Sc, Y) Solid Solutions

Synthesis and high-temperature phase transformation behavior of Dy2O3–Sc2O3 co-stabilized ZrO2 powders prepared by cocurrent chemical coprecipitation

Preparation and Characterization of Nanocrystalline Thin Films of Al2O3 or TiO2 Doped Scandia Stabilized Zirconia Solid Electrolytes

Preparations and Characterizations of New Mesoporous ZrO2 and Y2O3-stabilized ZrO2 Spherical Powders

Simultaneous precipitation of Zr4+ and Y3+ ions induced refinement of precursors and powders in fabrication of Zr4+ doped Y2O3 transparent ceramics

Phase Evolution, Texture Behavior, and Surface Chemistry of Hydrothermally Derived Scandium (hydrous) Oxide Nanostructures