Abstract:A boron-rich boron-carbide material (B4+δC) was synthesized by spark plasma sintering of a ball-milled mixture of high-purity boron powder and graphitic carbon at a pressure of 7 MPa and a temperature of 1930 °C. This high-pressure, high-temperature synthesized material was recovered and characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, Vickers hardness measurements, and thermal oxidation studies. The X-ray diffraction studies revealed a single-phase rhombohedral structure (space group R-3m) with lattice parameters in hexagonal representation as a = 5.609 ± 0.007 Å and c = 12.082 ± 0.02 Å. The experimental lattice parameters result in a value of δ = 0.55, or the composition of the synthesized compound as B4.55C. The high-resolution scans of boron binding energy reveal the existence of a B-C bond at 188.5 eV. Raman spectroscopy reveals the existence of a 386 cm-1 vibrational mode representative of C-B-B linear chain formation due to excess boron in the lattice. The measured Vickers microhardness at a load of 200 gf shows a high hardness value of 33.8 ± 2.3 GPa. Thermal gravimetric studies on B4.55C were conducted at a temperature of 1300 °C in a compressed dry air environment, and its behavior is compared to other high-temperature ceramic materials such as high-entropy transition metal boride. The high neutron absorption cross section, high melting point, high mechanical strength, and thermal oxidation resistance make this material ideal for applications in extreme environments.

High pressure and high temperature synthesis of a new boron carbide phase

Superhard solid solutions of diamond and cubic boron nitride

Direct Synthesis of Sp3‐hybridized BCN Compound by High Pressure and Temperature

Theoretical phase diagram of boron carbide from ambient to high pressure and temperature

High-pressure Phases of Boron Arsenide with Potential High Thermal Conductivity

Synthesis, Phase Evolutions, and Stabilities of Boron-Rich Tungsten Borides at High Pressure.

Design and Theoretical Study of Novel Multifunctional 3D-BC2N Polymorphs

Superhard sp<SUP>2</SUP>-sp<SUP>3</SUP> hybridized B<sub>2</sub>C<sub>3</sub>N<sub>2</sub> with 2D metallicity

Synthesis and Thermal Oxidation Resistance of Boron-Rich Boron-Carbide Material

High-Temperature High-Pressure Synchrotron X-Ray Diffraction Study Of C3n4

Phase transitions, mechanical properties and electronic structures of novel boron phases under high-pressure: A first-principles study

Superhard B–C–N materials synthesized in nanostructured bulks

Theoretical Study on the Controllable Preparation of Superhard BC2N under High Pressure

First principles study of post-boron carbide phases with icosahedra broken*

New Phase of Ca(BH4)2 at Near Ambient Conditions

Superhard and superconductive nondiamond-like BC structure

High-pressure Synthesis of Tungsten Carbide–cubic Boron Nitride (wc–cbn) Composites: Effect of Cbn Particle Size and Volume Fraction on Their Microstructure and Properties

Novel superhard boron nitrides, B2N3 and B3N3: Crystal chemistry and first principles studies

Crystal structures, elastic properties, and hardness of high-pressure synthesized CrB2 and CrB4

A New High Pressure and High Temperature Synthesis Idea Preparation of Micron Polycrystalline Transparent Cubic Boron Nitride

High-pressure synthesis of Al<sub>2</sub>O<sub>3</sub>-cBN composites: Effect of thermodynamic condition and cBN volume fraction on their microstructure and properties