Effects of B Addition on Microstructure Evolution and Efficient Hydrogen Evolution of Self‐Supported Cu–Fe–P Immiscible Alloy

Zhice Xu,Minghou Li,Chengcheng Xu,Chenghe Yan,Yan Ju,Tongtong Liu,Yan Wang,Degang Zhao,Min Zuo

DOI: https://doi.org/10.1002/adem.202400887

IF: 3.6

2024-09-09

Advanced Engineering Materials

Abstract:Herein, it is found that B element has a significant influence on the Marangoni motion of second‐phase in Cu–31.5Fe–4.5P immiscible alloy, resulting in the remarkable refinement of Fe2P and Fe3P secondary particles. The excellent hydrogen evolution reaction catalytic performance of samples can be attributed to the microstructure modification and the significant increase in the electron transfer with B addition. Herein, the effect of B elements on the microstructure and catalytic properties of Cu–31.5Fe–4.5P immiscible alloy is systematically investigated. After microstructure characterizations, it is found that B elements are mainly concentrated in FexP (Fe2P, Fe3P) particles, which affect the Marangoni motion of the particles. With the concentration of B content increasing to 0.75%, the diameter size of the second‐phase particles in the alloys is first refined and then coarsened, in which the alloy with B content of 0.25% has the finest particle size and the proportion of second‐phase particles with sizes ranging from 1 to 10 μm reaches 97%. The electrochemical characterization of dealloyed specimens shows that the overpotential of Cu–Fe–P alloys containing 0.25% B reaches 193 mV at a current density of 10 mA cm−2 in 0.5 m H2SO4 solution. The excellent catalytic performance might be attributed to the increase in the obviously specific surface area of Fe2P and Fe3P particles and the significant increase in the electron transfer.

materials science, multidisciplinary