Abstract:In order to obtain homogeneity and fine-scale microstructure of Cu–Fe alloy, a Cu-10 wt% Fe alloy slab was prepared by spray forming. The effects of cold rolling reduction on the alloy microstructure, mechanical properties, and electrical conductivity were studied. The results indicate that the Fe phase was fine and uniform with an average particle size of 4.16 μm, and the morphology of the particles was short rod or nearly spherical. The Cu matrix and Fe particles were gradually elongated, refined and finally formed into a distinct fiber structure along the rolling direction as the cold rolling reduction increased from 35 to 95%. The degree of deformation of the Cu matrix was more significant than that of the Fe phases at the same reduction, and more refined grains of the Cu matrix around the Fe phases. After cold rolling at 95% reduction, the Cu-10 wt% Fe exhibited an increase in tensile strength from 337 MPa in the initial state to 595 MPa, while the electrical conductivity decreased from 42.3% IACS to 20.2% IACS. The alloy deformation behavior and the strengthening mechanisms were illustrated. The combination of spray forming and cold rolling provides a novel approach to producing efficient, shortened process, environmentally friendly Cu–Fe alloy thin strips. Graphical A new process of preparing homogeneity and fine-scale microstructure Cu-10 wt% Fe alloy thin strip by spray forming and clod rolling is proposed. Fine and uniform Fe particles were obtained with an average size of 4.16 μm. Combined with the subsequent cold rolling, the effects of different reductions on the microstructure and mechanical properties after cold rolling were systematically studied. The specific abstract summary is as follows:

Microstructure Evolution and Performance of Cu–10Fe–2Ag–0·15Zr in Situ Composite by Cold Rolling

Attaining Exceptional Electrical Conductivity in Cu-Fe Composite by Powder Rolling Strategy

Achieving Homogeneous Fe Distribution and High Strength in Cu-Fe Composite Consolidated by Powder Rolling

Reforming Nanostructured CuAg Alloy to Improve Ductility and Electrical Conductivity

Managing Mechanical and Electrical Properties of Nanostructured Cu-Fe Composite by Aging Treatment

Microstructure evolution and properties of Cu–Ag microcomposites with different Ag content

Microstructure and Properties of Cold Drawing Cu-2.5% Fe-0.2% Cr and Cu-6% Fe Alloys

Effects on the Microstructure Evolution and Properties of Graphene/Copper Composite during Rolling Process

Deformation of Fe and Ag Precipitates in Cu Matrix

Microstructure and Properties of Cold Rolled Cu70Cr30 Composite

Effects of Cr addition on the microstructural, mechanical and electrical characteristics of Cu–6wt.%Ag microcomposite

Effect of Iron Content on the Strength and Conductivity of Cu-Fe In Situ Composite

Microstructure and strength of Cu–Fe–Ag in situ composites

Co-deformation in Cu–6 Wt.% Ag Nanocomposites

Properties of Cu and Fe under Large Deformation and Strength Calculation of Cu-11.5% Fe in Situ Composites

Effect of Fe Content on the Microstructure and Mechanical and Electrical Properties of Cu-Fe In Situ Composites

Microstructure and Properties of Cu–Fe Microcomposites with Prior Homogenizing Treatments

Microstructure and Properties of Heavily Drawn Cu-Ag-Fe Composites

Relationships between mechanical strength and electrical conductivity for Cu–Ag filamentary microcomposites

Microstructure Evolution and Property of Spray-Formed Cu-10 wt% Fe Alloy During Cold Rolling

Microstructure and Properties of Cu-Fe-Ag In-Situ Composites