Abstract:The effect of composition tuning on glass forming ability (GFA), mechanical properties and atomic structure in ZrxCo84−xAl16 bulk metallic glasses (BMGs) with x = 51–58 has been investigated by using copper-mold suction casting, nanoindentation, high-energy X-ray diffraction, extended X-ray absorption fine structure experiments and ab initio molecular dynamics simulations, respectively. It is found that GFA firstly increases then decreases with increasing Zr content, exhibiting a maximum diameter of 7 mm with the Zr content of 55 and 56, while an abrupt reduction of bending plasticity occurs as the Zr content drops below 55. Both experimental and theoretical results find that GFA is remarkably enhanced, due to the abnormal reduction in the fractions of the Co-centered ⟨0, 2, 8, 1⟩, ⟨0, 3, 6, 2⟩ and ⟨0, 3, 6, 3⟩ polyhedra, and the denser atomic packing of Zr atoms around center Co atom, as the Zr content increases from 51 to 56. Meanwhile, the simultaneously improved plasticity is associated with the increased Co-centered ⟨0, 3, 6, 0⟩, and Al-centered ⟨0, 2, 8, 1⟩ and ⟨0, 3, 6, 2⟩ polyhedra, which provide more fertile sites for the nucleation of shear transformations. Further Zr addition to 58 increases remarkably the fractions of Zr- and Al-centered ⟨0, 1, 10, 2⟩ and ⟨0, 3, 6, 4⟩ polyhedra, and causes looser atomic packing of Co atoms around center Zr atom, leading to the reduction in GFA. However, the plasticity is not enhanced further but remains nearly constant, which may be related to the deteriorated effect on plasticity of the decreased fractions of Zr-centered ⟨0, 1, 10, 5⟩ and Co-centered ⟨0, 3, 6, 0⟩ polyhedra, and the increased fractions of Zr-centered ⟨0, 1, 10, 3⟩ and ⟨0, 2, 8, 4⟩ and Co-centered ⟨0, 2, 8, 0⟩ polyhedra. Compositional tuning, with internal structure tuned to favor both GFA and plastic flow, offers new possibilities in developing ductile BMG materials.

Ni- and Cu-free Zr–Al–Co–Ag bulk metallic glasses with superior glass-forming ability

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

Ni-free Zr-based bulk metallic glasses with critical diameter above 20mm

Glass Forming Ability and Corrosion Resistance of Zr-Cu- Ni-Al-Ag Bulk Metallic Glass

Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses

Synthesis of Centimeter-Size Ag-doped Zr–Cu–Al Metallic Glasses with Large Plasticity

Biocompatibility of Ni-free Zr-based Bulk Metallic Glasses

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

Glass forming ability and bending plasticity evolutions in Zr-Co-Al bulk metallic glasses and their structural origin

Glass Forming Ability and Crystallization of Zr–Cu–Ag–Al–Be Bulk Metallic Glasses

Enhancing strength and plasticity of Zr-based bulk metallic glasses by Zr partially substituted Fe and isothermal annealing

Zr–Ti–Al–Fe–Cu bulk metallic glasses for biomedical device application

Formation and properties of biocompatible Ti-based bulk metallic glasses in the Ti–Cu–Zr–Fe–Sn–Si–Ag system

La-based bulk metallic glasses with critical diameter up to 30mm

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Incorporation of ultrafine nanograins in Zr–Cu–Al–Ni–Co bulk metallic glass enabling significantly improved mechanical properties

Effect of Ag substitution for Ti on glass-forming ability, thermal stability and mechanical properties of Zr-based bulk metallic glasses

Fe–C micro-alloying effect on properties of Zr53Al11.6Ni11.7Cu23.7 bulk metallic glass

73 Mm-Diameter Bulk Metallic Glass Rod By Copper Mould Casting

In Vitro Investigation of Novel Ni Free Zr-based Bulk Metallic Glasses As Potential Biomaterials

The effect of minor alloying on the glass forming ability and crystallization reaction of Ti32.8Zr30.2Cu9M5.3Be22.7 (M=Fe, Co, and Ni) bulk metallic glass