Abstract:A series of Zr63.5−xTixAl9Fe4.5Cu23 (x = 0, 1.5, 3.0, 4.5, 6.0; at%) bulk metallic glasses (BMGs) were designed and produced by means of copper mold suction casting. The effect of Ti addition on the glass-forming ability (GFA) and mechanical properties of Zr63.5−xTixAl9Fe4.5Cu23 alloys was first investigated. The glass-forming ability and room-temperature plasticity of BMGs increase first and then reduced with Ti content increasing. At x = 3.0, the Zr60.5Ti3Al9Fe4.5Cu23 BMG showed a critical glass formation diameter of 10 mm and excellent room-temperature compressive plasticity (ɛP = 4.7%) by using the samples with dimensions of Φ3 mm × 6 mm. Meanwhile, the BMG also showed better biocompatibility and biocorrosion resistance compared with Ti6Al4V alloy. Under the imitated human body condition, the corrosion current density (Icorr) of BMG was 6.61 × 10–10 A·cm−2, which is two orders of magnitude lower than that of conventional Ti6Al4V alloy. Moreover, the CCD-986sk cell viabilities are, respectively, 65.4% and 46.6% on the BMG and Ti6Al4V alloy, indicating better biocompatibility of BMG. The Zr60.5Ti3Al9Fe4.5Cu23 BMG with larger GFA, excellent mechanical properties, biocompatibility and biocorrosion resistance is considered as a potential material in biomedical device fields.Graphic abstract

What problem does this paper attempt to address?

The paper primarily explores the potential of Zr-Ti-Al-Fe-Cu Bulk Metallic Glasses (BMGs) in biomedical device applications. The authors designed and prepared a series of Zr63.5-xTixAl9Fe4.5Cu23 BMGs with varying titanium content (x = 0, 1.5, 3.0, 4.5, 6.0 at%) using the copper mold suction casting method, and investigated the effect of titanium addition on the glass-forming ability and mechanical properties of these alloys. Specifically, the paper addresses the following key issues: 1. **Glass Forming Ability (GFA)**: As the titanium content increased from x = 0 to x = 3.0, the critical glass-forming diameter (d_max) of the alloy increased from 6mm to 10mm; however, when the titanium content further increased to x = 6.0, d_max significantly decreased to 3mm. The Zr60.5Ti3Al9Fe4.5Cu23 alloy exhibited the best GFA. 2. **Room Temperature Plasticity**: The Zr60.5Ti3Al9Fe4.5Cu23 alloy demonstrated excellent room temperature compressive plasticity (ε_P = 4.7%), which is better than other alloys. 3. **Biocompatibility and Biocorrosion Resistance**: Compared to the traditional Ti6Al4V alloy, the Zr60.5Ti3Al9Fe4.5Cu23 alloy showed better biocompatibility and lower corrosion current density (I_corr = 6.61×10^-10 A/cm^2), indicating superior biocorrosion resistance. 4. **Cell Viability**: Under simulated human conditions, the cell viability of CCD-986sk cells on the Zr60.5Ti3Al9Fe4.5Cu23 alloy was 65.4%, while it was only 46.6% on the Ti6Al4V alloy. In summary, the Zr60.5Ti3Al9Fe4.5Cu23 alloy is considered a highly promising material in the field of biomedical devices due to its high glass-forming ability, excellent mechanical properties, good biocompatibility, and biocorrosion resistance.

Zr–Ti–Al–Fe–Cu bulk metallic glasses for biomedical device application

Antimicrobial Zr-based bulk metallic glasses for surgical devices applications

Formation and properties of biocompatible Ti-based bulk metallic glasses in the Ti–Cu–Zr–Fe–Sn–Si–Ag system

Biocompatibility of Ni-free Zr-based Bulk Metallic Glasses

In Vitro Cytocompatibility of a Zr-based Metallic Glass Modified by Laser Surface Texturing for Potential Implant Applications

Biocompatibility of a micro-arc oxidized ZrCuAlAg bulk metallic glass

Zr–(Cu,Ag)–Al Bulk Metallic Glasses

In Vitro Study On Zr-Based Bulk Metallic Glasses As Potential Biomaterials

Ni-Free Zr-Based Bulk Metallic Glasses with Critical Diameter above 20 Mm

Ti40Zr10Cu36Pd14 bulk metallic glass as oral implant material

Cu-Zr-Al-Ti bulk metallic glass with enhanced glass-forming ability, mechanical properties, corrosion resistance and biocompatibility

Fabrication and comprehensive evaluation of Zr-based bulk metallic glass matrix composites for biomedical applications

Glass-Forming Ability, Mechanical Properties, and Energetic Characteristics of ZrCuNiAlNbHfY Bulk Metallic Glasses

In Vitro Investigation of Novel Ni Free Zr-based Bulk Metallic Glasses As Potential Biomaterials

Nontoxic, precious-metal-free titanium-based metallic glasses with exceptional glass-forming ability and high specific strength

A Ti–Zr–Be–Fe–Cu Bulk Metallic Glass with Superior Glass-Forming Ability and High Specific Strength

Open-Cell Tizr-Based Bulk Metallic Glass Scaffolds with Excellent Biocompatibility and Suitable Mechanical Properties for Biomedical Application

Centimeter-sized Ti-rich Bulk Metallic Glasses with Superior Specific Strength and Corrosion Resistance

Deformation behavior, corrosion resistance, and cytotoxicity of Ni-free Zr-based bulk metallic glasses

Osteogenesis and angiogenesis of a bulk metallic glass for biomedical implants

Lightweight Ti–Zr–Be–Al Bulk Metallic Glasses with Improved Glass-Forming Ability and Compressive Plasticity