Application of High Magnetic Field to Lessen the Strength Dispersion of Carbon Fiber
Xiaomeng Ren,Yuansheng Wang,Te He
2012-01-01
Abstract:Strength dispersion is one of the main problems that restrained the development of carbon fiber.In order to lessen dispersion,8 T,12 T,16 T high magnetic fields were applied to the pre-oxidized carbon fiber(CF).And the carbon fibers were measured by small angle X-ray scattering(SAXS),nitrogen isothermal adsorption and desorption,monofilament tensile experiment,scanning electron microscope(SEM).The results show that,by the induction of magnetic field,the percentage of macroscopic internal voids decreases to 21%,14%,11% and the number of external voids decreases by 9.80%,13.47%,15.10%,respectively.And the effect is enhanced as the magnetic field intensity increasing.Through Weibull statistics,it was found that average strength increases by 3.4%,5.7%,8.4% respectively.Furthermore,the magnetic field lessens strength dispersion of CF and coefficient of variation(CV) is 0.326,0.308,0.306 respectively.