Effect of high magnetic field annealing on carbon diffusion in γ-iron

Yan Wu,Yan Lu,ZhiJia Wang

2012-01-01

Abstract:The effect of high magnetic field annealing on carbon diffusion behavior in γ-Fe was investigated by varying the angles between the magnetic field direction and the carburizing direction. High purity iron samples were subjected to isothermal annealing at 930°C for 25 min with or without the magnetic field. The results showed that the average carbon diffusion distance of the samples carburized with the high magnetic field is much less than that of the corresponding samples carburized without the magnetic field, which indicates that the magnetic field annealing obviously hinders the carbon diffusion behavior in pure iron in the single-phase austenite region at 930°C. For the samples carburized with the high magnetic field, there is only a small change in the average carbon diffusion distance by varying the angles between the magnetic field direction and the carburizing direction, which suggests that there is no obvious effect for the carbon diffusion in pure iron when varying the magnetic field directions in the high magnetic field at 930°C.