Preparation and Characterization of LaPO4: Eu3+ @ SiO2 Core-shell Luminescent Naonrods

LIU Gui-xia,LI Ruo-lan,DONG Xiang-ting,WANG Jin-xian

DOI: https://doi.org/10.3788/fgxb20113205.0466

2011-01-01

Chinese Journal of Luminescence

Abstract:LaPO_4:Eu~(3+)luminescence nanorods were prepared via a hydrothermal method without any surfactants, then an uniform SiO_2 layer was coated on the surface of LaPO_4:Eu~(3+)nanorods by sol-gel method.At lasts LaPO_4:Eu~(3+)@ SiO_2 core-shell structural luminescence nanorods were achieved.XRD patterns show that the uncoated and coated samples are all monclinic LaPO_4 crystals.FTIR spectra indicate that LaPO_4:Eu~(3+)is linked with SiO_2 by chemical bond.TEM images reveal that the LaPO_4:Eu~(3+)samples are one-dimensional nanorods with a diameter of 20 nm and a length of 300～500 nm.The coating thickness of SiO_2 can be controlled by the concentration of TEOS.The results of photoluminescence properties show that the main emission peak of LaPO_4:Eu~(3+)nanorods is near 591 nm,which is the characteristic orange red light corresponding to ~5D_0→~7E_1 transition of Eu~(3+)under 259 nm excitation.The PL intensity of the samples become weak with the increasing of the coating thickness,but the shape and the position of the peaks are not changed.