Abstract:In this paper, a new process for the phase-separated P2O5-Al2O3 glass with SiO2-rich region is presented. The new method combines pneumatic atomization with mechanical stirring based on melting-quenching preparation. X-ray diffraction, Nano-infrared spectra, X-ray photoelectron spectra, Raman scattering spectra and atomic force microscope were carried out to investigate sample's structure and surface morphology. The results show that the phase-separated glasses consist of second phase, transition region and matrix region. The average diameter of separated phase, ie. 500 nm, 150 nm, 76 nm and 85 nm, depends on the diameter of SiO2 glass particles prepared by ball milling, that is 50 mu m, 10 mu m, 2 mu m and 400 nm respectively. Especially, transition region is formed by the connection of phosphorus oxygen tetrahedron and silicon oxygen tetrahedron, located between SiO2 region and matrix network region. After introducing the second phase, the Young's modulus of matrix glass was increased by 32.5% and the optimal value is 77.67 GPa within the scope of this experiment. It is attributed to that the formation of transition region increases the cross-linking of P2O5-Al2O3 glass network. The Young's modulus of the phase-separated glass increases with the diameter of the quartz glass particles decreases from 50 mu m to 2 mu m, but weakens at a diameter of 400 nm. The network polymerization due to increasing in the number of P3 units induced by second phase's diameter is responsible for rising in the Young's modulus, whereas too low diameter leads to particle agglomeration accompanied by the present of defects.

Preparation of nano-SiO 2 using melting method

PREPARATION OF NiO NANOPARTICLES ON THE SILICA SURFACE BY ADSORPTION PHASE SYNTHESIS AND ITS REGULATION ON MORPHOLOGY OF NiO PARTICLES

Synthesis, Characterization and Application of Submicron ZrSiO4 Powder Via Sol-Gel-microemulsion-hydrothermal Method

Preparation and Characterization of Nano-Sized SiO2 Particles by Microemulsion Method

Synthesis of Disperse Amorphous SiO2 Nanoparticles Via Sol–gel Process

Preparation of Nano Silicon Dioxide with Sol-Gel Method

The Preparation Process Design of Loaded Nanometer Oxide Material

Study on Phase Separation and Crystallization of Na2O-B2O3-SiO2-TiO2 Glass

High-surface-area Disperse Silica Nanoparticles Prepared Via Sol-Gel Method Using L-lysine Catalyst and Methanol/water Co-Solvent

Synthesis of Mesoporous SiO2 Glass by a Novel Chemical Method

Preparations of SiS and SiO2 nanospheres

Disperse Ultrafine Amorphous SiO2 Nanoparticles Synthesized Via Precipitation and Calcination

A Novel Method for Preparing Phase-Separated P2O5–Al2O3 Glass with High Young's Modulus

In-Situ Control of CaO-MgO-SiO2 Nanoparticles Synthesized by the Sol-Gel Method

Controllable Preparation of Sio2 Nanoparticles Using A Microfiltration Membrane Dispersion Microreactor

Preparation of Nanoporous Silicon and Study on Its Properties

Preparation of nano-silica powder from silica sand via sol-precipitation method

Preparation of Nano Silica and Its Application in the Environmental Field

Research on the preparation of nano SiO 2-Al 2O 3-TiO 2 particle

Preparation and In-situ Modification of Nanometer SiO_2 by Chemical Precipitation Method

Preparation and surface modification of nano-silica