Abstract:The synthesis of magnetic particles triggers the interest of many scientists due to their relevant properties and wide range of applications in the catalysis, nanomedicine, biosensing and magnetic separation fields. A fast synthesis of iron oxide magnetic particles using an eco-friendly and facile microwave-assisted solvothermal method is presented in this study. Submicron Fe3O4 spheres were prepared using FeCl3 as an iron source, ethylene glycol as a solvent and reductor and sodium acetate as a precipitating and nucleating agent. The influence of the presence of polyethylene glycol as an additional reductor and heat absorbent was also evaluated. We reduce the synthesis time to 1 min by increasing the reaction temperature using the microwave-assisted solvothermal synthesis method under pressure or by adding PEG at lower temperatures. The obtained magnetite spheres are 200-300 nm in size and are composed of 10-30 nm sized crystallites. The synthesized particles were investigated using the XRD, TGA, pulsed-field magnetometry, Raman and FTIR methods. It was determined that adding PEG results in spheres with mixed magnetite and maghemite compositions, and the synthesis time increases the size of the crystallites. The presented results provide insights into the microwave-assisted solvothermal synthesis method and ensure a fast route to obtaining spherical magnetic particles composed of different sized nanocrystallites.

Microwave Assisted Solvothermal Synthesis of Magnetic Fe3o4 Micro Spheres and Spherical Aggregates at Low Temperature

Microwave Fabrication and Magnetic Property of Hierarchical Spherical Α-Fe2o3 Nanostructures

Microwave-solvothermal synthesis of Fe3O4 magnetic nanoparticles

Microwave-Assisted Solvothermal Synthesis of Nanocrystallite-Derived Magnetite Spheres

Magnetic Properties of Nano-structure Fe3O4 Hollow Microspheres by Solvothermal Method

Synthesis of Highly Dispersed Fe3O4 Submicrometer Spheres in a One-Pot Anion-induced Solvothermal System

Synthesis and microwave absorption properties of hollow Fe3O4 microspheres

Solvothermal Synthesis and Magnetic Property of Monodispersed Fe_3O_4 Nano-powders

Formation Mechanism and Magnetic Properties of Hollow Fe3o4 Nanospheres Synthesized Without Any Surfactant

A Time-Saving Method to Prepare Monodisperse Fe3O4 Microspheres with Controllable Sizes and Morphologies

Synthesis of Monodisperse and Single-Crystal Fe3o4 Hollow Spheres by A Solvothermal Approach

Synthesis of crystal MFe2O4 (M = Mg, Cu, Ni) microspheres

Synthesis of maghemite sub-microspheres by simple solvothermal reduction method

Novel Fe3o4 Hollow Microspheres: Nontemplate Hydrothermal Synthesis, Superparamagnetism and Biocompatibility

Synthesis and Characterization of Hollow Fe 3 O 4 Submicrospheres by a Simple Solvothermal Synthesis

A facile solvothermal synthesis and magnetic properties of MnFe 2 O 4 spheres with tunable sizes

Solvothermal Synthesis of Magnetic Fe3o4 Microparticles Via Self-Assembly of Fe3o4 Nanoparticles

Microwave-assisted Solution-Phase Preparation and Growth Mechanism of FeMoO4hierarchical Hollow Spheres

Hierarchically Nanostructured Fe3O4 Microspheres and Their Novel Microwave Electromagnetic Properties

Controlled Synthesis of Spherical and Cubic Magnetite Nanocrystal Clusters

Synthesis and Magnetic Properties of Nano-structure Fe_3O_4 Hollow Microspheres