Abstract:Monodispersed magnetic MFe2O4 (M = Fe, Co) hollow spheres were synthesized by simple template free solvothermal method in ethylene glycol (EG) solution. The hollow spheres were in the same size with an average diameter of about 360 nm and the shells of these spheres were about 80 nm, consisted of closely packed nanocrystallines due to Ostwald ripening. EG plays the key role in the synthesis of hollow spheres in contrast with octahedral crystals synthesized in aqueous solution. The products synthesized in aqueous solution were calcined at 800 degrees C and 1000 degrees C. The amount of spinel ferrite products increased monotonically with the increase of temperature and appeared as a single phase at 1000 degrees C. The saturation magnetization (M-s), remanent magnetization (M-r) and coercivity (H-c) for Fe3O4 hollow spheres was 74.47 emu/g, 2.59 emu/g and 32.503 Oe respectively whereas the reading of the same indicators for CoFe2O4 hollow spheres was 69.07 emu/g, 14.46 emu/g and 242.79 Oe, respectively. The magnetic variation between Fe3O4 and CoFe2O4 hollow spheres was caused by the radius difference of Fe2+ (3d(6)) and Co2+ (3d(7)) ions and it was also relevant with nanocrystal sizes of the spin disorder of crystal surface. Crown Copyright (C) 2011 Published by Elsevier B.V. All rights reserved.

Synthesis of crystal MFe2O4 (M = Mg, Cu, Ni) microspheres

A facile solvothermal synthesis and magnetic properties of MnFe 2 O 4 spheres with tunable sizes

Synthesis of Highly Dispersed Fe3O4 Submicrometer Spheres in a One-Pot Anion-induced Solvothermal System

Synthesis of maghemite sub-microspheres by simple solvothermal reduction method

A Time-Saving Method to Prepare Monodisperse Fe3O4 Microspheres with Controllable Sizes and Morphologies

Synthesis of Monodisperse and Single-Crystal Fe3o4 Hollow Spheres by A Solvothermal Approach

Solvothermal synthesis and characterization of NiFe2O4 nanospheres with adjustable sizes

Facile Ultrafast Microwave Synthesis of Monodisperse MFe 2 O 4 (m=fe, Mn, Co, Ni) Superparamagnetic Nanocrystals

Synthesis and Characterization of Hollow Fe 3 O 4 Submicrospheres by a Simple Solvothermal Synthesis

Synthesis of Mgfe2o4 Nanocrystallites under Mild Conditions

Preparation and characterization of monodispersed Fe3O 4 sub-microspheres | Preparation and characterization of monodispersed Fe3O 4 sub-microspheres

Synthesis and Characterization of Monodisperse Fe3O4Nanospheres with Uniform Particle Size Distribution by a Simple Solvothermal Method

Large-Scale Synthesis of Uniform Spinel Ferrite Nanoparticles from Hydrothermal Decomposition of Trinuclear Heterometallic Oxo-Centered Acetate Clusters

Size-controlled synthesis and magnetic properties of NiFe2O4 hollow nanospheres via a gel-assistant hydrothermal route

Diameter and Aggregation Controlled Preparation by Solvothermal Synthesis of Ultra-small Particles CuFe$_2$O$_4$

Synthesis And Characterization Of Nanosized Mgfe2o4 Powders By Hydrothermal Method

One-Step Synthesis of Mfe2o4 (M = Fe, Co) Hollow Spheres by Template-Free Solvothermal Method

Nonstoichiometric M-ferrite Porous Spheres: Preparation, Shape Evolution and Magnetic Properties

Solvothermal synthesis and characterization of size-controlled monodisperse Fe 3 O 4</s

Large-scale synthesis and characterization of monodisperse Fe3O4 nanocrystals

Size Controllable Synthesis of Magnetite Fe3O4 Nanoparticles