Abstract:Aiming at developing carbon fibre/polyamide-12 (CF/PA) composite powders for manufacturing high-performance components by selective laser sintering (SLS), the preparation, characteristics and sintering process of the composite powders and mechanical properties of sintered components were studied. Surfaces of the carbon fibres were treated by the oxidation modification and coated with polyamide-12 through the dissolution-precipitation process to provide good interfacial adhesion and homogenous dispersion within the polyamide-12 matrix. The particle size and micro-morphology analyses show that the CF/PA composite powders with 30 wt%, 40 wt% and 50 wt% carbon fibres present the suitable powder sizes and format for SLS. The incorporation of carbon fibres into the polyamide-12 matrix decreases the initial melting temperature and consequently lowers the SLS part bed temperatures, implying lower energy requirement and less thermal degradation in the sintering process. The CF/PA composites also represent higher thermal stability than the pure polyamide-12. The CF/PA sintered components with 30 wt%, 40 wt% and 50 wt% carbon fibres exhibit the greatly enhanced flexural strengths by 44.5%, 83.3%, 114%, and the flexural modulus by 93.4%, 129.4%, 243.4%, respectively, as compared with the pure polyamide-12 sintered parts. Fractured surface analysis shows that the carbon fibres are encapsulated and bonded well with the polyamide matrix. The complex SLS parts with the thinnest wall of 0.6 mm, the density of 1.09 +/- 0.02 g/cm(3) and the relatively density of 94.13 +/- 1.72% were manufactured using the CF/PA composite powder with 30 wt% carbon fibres. This study demonstrates that the CF/PA composite powders prepared by the surface treatment and dissolution-precipitation method represent suitable interfacial adhesion, filler dispersion, particle sizes and sintering behaviours for SLS and enable the manufacture of complex components with high performance. (C) 2011 Elsevier Ltd. All rights reserved.

Preparation, Characterisation and Processing of Carbon Fibre/polyamide-12 Composites for Selective Laser Sintering

Characterisation Of Carbon Fibre Reinforced Nylon-12 Composites For Selective Laser Sintering Process

A Novel Method Based on Selective Laser Sintering for Preparing High-Performance Carbon Fibres/polyamide12/epoxy Ternary Composites

Surface modification of carbon fibers and the selective laser sintering of modified carbon fiber/nylon 12 composite powder

Preparation and selective laser sintering behavior of carbon fiber/polyamide 1 2 composite

Selective laser sintering of polyamide 12 composites

Preparation and Selective Laser Sintering of Nylon-12-Coated Aluminum Powders

Effect of Fabrication Process on the Microstructure and Mechanical Performance of Carbon Fiber Reinforced PEEK Composites Via Selective Laser Sintering

Fabrication Process and Properties of Porous Polyamide Produced by Selective Laser Sintering

High Temperature Rheological Behavior and Sintering Kinetics of CF/PEEK Composites During Selective Laser Sintering

Preparation and Laser Sintering of Limestone PA 12 Composite

Selective Laser Sintering of Polyamide 12/potassium Titanium Whisker Composites

Preparation of PA11/BaTiO3 Nanocomposite Powders with Improved Processability, Dielectric and Piezoelectric Properties for Use in Selective Laser Sintering

Hybrid of multi‐dimensional fillers for thermally enhanced polyamide 12 composites fabricated by selective laser sintering

Selective Laser Sintering of Aluminum/nylon 12 Composite Powder

Inorganic Fullerene-Like WS2 Reinforced Polyamide Powders for Improved Mechanical Properties in Laser Sintered Nanocomposite Parts

Selective Laser Sintering Parameter Optimization of Prosopis Chilensis/Polyethersulfone Composite Fabricated by AFS-360 SLS

Progress on Selective Laser Sintering of Polymers and Polymer Composites

Properties of oriented carbon fiber/polyamide 12 composite parts fabricated by fused deposition modeling

Microstructure of Selective Laser Sintered Polyamide

The Combination of Al2O3 and BN for Enhancing the Thermal Conductivity of PA12 Composites Prepared by Selective Laser Sintering.