Preparation and selective laser sintering behavior of carbon fiber/polyamide 1 2 composite

Qiong WU,Hui CHEN,Jing WU,Xiaohong XIA,Xiaoshu XU,Hong BIAN,Hongbo LIU

DOI: https://doi.org/10.3969/j.issn.1001-9731.2016.04.035

2016-01-01

Abstract:The PAN-based chopped carbon fibers were surface modified by liquid-phase oxidation,mixed with polyamide 12,and the carbon fiber reinforced polyamide 12 composites were prepared by selective laser sinte-ring technology.Scanning electron microscope and Fourier transform infrared spectrum were applied to the characterization of the surface state on the carbon fibers before and after modification,the dispersity of compos-ite powder,and fracture morphology of the sintered components.The sintering behavior of composite powder, the relationship between mechanical property and porosity of the sintered components were also discussed.The results show that the oxygen-containing groups on the surface of modified carbon fibers are thermal decomposed and release gas in the process of laser sintering,which cause a high porosity and poor mechanical properties of the sintered components.While the carbon fibers treated under high temperature after modification can preserve the surface roughness,lower the porosity at the same time,and compared with the unmodified carbon fiber re-inforced polyamide 1 2 sintered components,the tensile strength,tensile modulus,flexural strength,flexural modulus are incresed at different degrees.