Damage process of composite aero-engine case impacted by blade

Lulu Liu,Haijun Xuan,Qing He,Jun Xing,Jin Wang

2011-01-01

Abstract:To investigate the failure mechanism of a kind of 2D tri-axial braid carbon fiber reinforced composite fan case, a blade/case containment test was carried out in the high-speed spin tester and its numerical simulation based on continuum damage constitutive mechanics was conducted also. The numerical simulation results are in good agreement with the test results. The results indicate that the fiber shear fracture, matrix shear failure and matrix crush failure occur in the inner wall of the case, while the fiber tensile failure, fiber pull-out, matrix cracking and delamination failure occur in the outer wall. There are three continuous impacts between the blade and case during the containment process. The blade's kinetic energy is absorbed mostly in the first impact, which causes the case's extensive damage and failure.