Abstract:Nickel-based single crystal superalloys, as engine blade materials, are prone to fatigue damage due to repeated startups and shutdowns. Therefore, monitoring and quantitatively estimating fatigue cracks are essential for engineering structures to ensure safety. In this study, we proposed a method for fatigue crack segmentation and damage prediction based on deep learning and in-situ high-temperature scanning electron microscopy (SEM). Sequential SEM images describing the crack initiation and propagation under near-service conditions were obtained by conducting in-situ high-temperature fatigue experiments. A fatigue crack dataset with high-quality was thus constructed for further dynamic and real-time crack segmentation and damage assessment. Deep learning-based models were used to segment cracks and predict damage behavior (i.e., crack area, length, width, and stress intensity factors) at future based on prior damage information. The short-term and long-term damage prediction capability were validated by comparing model performance when predicting damage at different future time points. Additionally, we compared the model performance when predicting damage at specific time point based on varying lengths of input sequence. Results demonstrated that the model could segment cracks and scales with different sizes accurately. The model performed well in short-term damage prediction. The long-term predictive performance showed decrease than that of short-term, which could be improved by feeding long length of input sequence. The proposed approach demonstrates the feasibility and effectiveness of deep learning-based crack segmentation and damage prediction, which facilitates the move toward real-time analysis and rapid diagnosis of material damage in the future.

Fish-Eye Shape Prediction with Gigacycle Fatigue Failure

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Improvement Of Cyclic Void Growth Model For Ultra-Low Cycle Fatigue Prediction Of Steel Bridge Piers

Effect of fisheye failure on material performance inducing error circle under high cycles

Surface Vs. Interior Failure Behaviors in a Structural Steel under Gigacycle Fatigue: Failure Analysis and Life Prediction

A Hybrid Modeling Method of Fatigue Crack Growth for Gas Turbine Blades under Combined High and Low Cycle Fatigue Loadings

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

Prediction of Fatigue Life for Automotive A-Alloy Wheel with Integrated Cast Defects

Prediction of Fatigue Crack Damage Using In-Situ Scanning Electron Microscopy and Machine Learning

A New Empirical Life Prediction Model For 9-12%Cr Steels Under Low Cycle Fatigue And Creep Fatigue Interaction Loadings

Prediction of Low Cycle Fatigue Crack Growth under Mixed-mode Loading Conditions Using Cohesive Zone Models

Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors

Prediction of fatigue crack growth life based on a new fusion model

Fatigue life prediction driven by mesoscopic defect data

The whole fatigue crack propagation life prediction of Ni-based single crystal super-alloy specimen with single hole based on EIFS and ‘Fish-eye’ theory

Fatigue life assessment of nickel-based single crystals considering equivalent initial flaw size model and anisotropy

Fatigue life prediction at mesoscopic scale of samples containing casting defects: A novel energy based non-local model

A Combined High and Low Cycle Fatigue Model for Life Prediction of Turbine Blades

Fractographic Analysis and Particle Filter-Based Fatigue Crack Propagation Prediction of Q550E High-Strength Steel

A data-physics integrated approach to life prediction in very high cycle fatigue regime

A Two‐Scale Model of Fretting Fatigue Crack Initiation Life Based on Long Short‐Term Memory Networks Improved by Genetic Algorithm