Abstract:Mechanical properties of metallic materials gradually degrade under high-temperature low cycle fatigue (HTLCF) loading, which is a manifestation of fatigue damage accumulation. In this study, a mapping modeling is developed to determine the relationship between micro-scale HTLCF damage and macro-scale mechanical property degradation. Strain-controlled HTLCF tests in GH4169 superalloy are carried out at 650 °C and interrupted at various lifetime fractions for subsequent microscopic characterizations and high-temperature tensile tests. Quantitative analysis of electron backscatter diffraction indicates a three-stage increase in kernel average misorientation and geometrically necessary dislocation throughout the cyclic process, along with variations in the fraction of different grain boundaries. Simultaneously, the evolutions of shearing precipitate and de-twinning are characterized using transmission electron microscope. Furthermore, the mechanical properties of GH4169 superalloy, such as yield strength, ultimate tensile strength, elongation and work-hardening rate, demonstrate different degradation characteristics after exposure to HTLCF damage. Based on these results, the mechanism of HTLCF-induced mechanical property degradation is clarified and the mapping modeling is established using tensile plastic strain energy density and kernel average misorientation. Finally, a damage level evaluation method for engineering components is developed after the generality and flexibility of model is verified in different high-temperature materials.

Effect of fisheye failure on material performance inducing error circle under high cycles

Improvement Of Cyclic Void Growth Model For Ultra-Low Cycle Fatigue Prediction Of Steel Bridge Piers

A Model for Ultra Low Cycle Fatigue Damage Prediction of Structural Steel

Ultra-low Cycle Fatigue Evaluation Method for Unstiffened Steel Piers Using Fiber Model

Effect Of Corroded Surface Morphology On Ultra-Low Cycle Fatigue Of Steel Bridge Piers

Improved Ultra-Low Cycle Fatigue Fracture Models for Structural Steels Considering the Dependence of Cyclic Damage Degradation Parameters on Stress Triaxiality

A Proposal on Ultra-Low Cycle Fatigue Damage Evaluation of Structural Steels

Fish-Eye Shape Prediction with Gigacycle Fatigue Failure

A Modified Coffin-Manson Model for Ultra-Low Cycle Fatigue Fracture of Structural Steels Considering the Effect of Stress Triaxiality

Very High Cycle Fatigue Failure Analysis and Life Prediction of Cr-Ni-W Gear Steel Based on Crack Initiation and Growth Behaviors

Surface Vs. Interior Failure Behaviors in a Structural Steel under Gigacycle Fatigue: Failure Analysis and Life Prediction

Multiaxial high-cycle fatigue failure and life prediction based on critical plane method

The whole fatigue crack propagation life prediction of Ni-based single crystal super-alloy specimen with single hole based on EIFS and ‘Fish-eye’ theory

Microstructure-Based Fatigue Modeling with Residual Stresses: Effect of Inclusion Shape on Very High Cycle Fatigue Life

Characterization and application of maximum entropy fatigue damage model based on digital image correlation and inverse analysis

Experimental and computational investigation of weathering steel Q450NQR1 under high cycle fatigue loading via crystal plasticity finite element method

Development of improved Manson-Coffin model considering the effect of yield stress under asymmetrical cyclic loading

Experimental and Numerical Study of Combined High and Low Cycle Fatigue Performance of Low Alloy Steel and Engineering Application

An engineering model of fatigue crack growth under variable amplitude loading

Determination of relationship between high-temperature low cycle fatigue damage and mechanical property degradation: Experimental and theoretical analyses

Influence of Non-Metallic Inclusions on Very High-Cycle Fatigue Performance of High-Strength Steels and Interpretation via Crystal Plasticity Finite Element Method