Abstract:The presence of cracks on pipelines poses a potential threat to their operational status, and it is critical to assess the permissibility of pipelines containing cracks. The dimensional analysis combined with the finite element method is applied to investigate the fracture behavior of circumferential crack on the internal surface of pipe under internal pressure and large axial deformation. Dimensionless parameters are determined to represent the effects of crack size, pipe geometry, pipe material, and external load on the crack front driving force, and a strain-based J-integral formulation is obtained by a stepwise coefficient fitting approach rather than a polynomial fitting method. This J-integral formula can be used to quickly assess the crack front driving force of a pipe in service condition and subjected to axial displacement. The diameter-to-thickness ratio of the pipe and the dimensionless pressure of the pipe are found to act together in a combined form on the crack front driving force. Increases in dimensionless crack depth, dimensionless crack length, the ratio of circumferential stress to yield strength of the pipe, and strain hardening exponent cause an increase in the crack front driving force. The effect of dimensionless crack depth on crack front driving force is more significant than other dimensionless parameters. Changes in the other dimensionless parameters do not significantly change the crack front driving force when the dimensionless crack depth is small. Other dimensionless parameters have a progressively greater influence on the crack front driving force as the crack dimensionless crack depth increases. Large deformations in the ligament zone and increasing axial stress are the main reasons for the high crack front driving force. The J-integral formula has a similar form to that of the J-integral in the Electric Power Research Institute (EPRI) method when the effect of internal pressure is not considered. It can be reduced to predict the crack front driving force of a surface cracked plate subjected to uniaxial tensile loading. For the interaction between an internal surface crack and an embedded crack, re-characterizing the crack size using BS 7910 will overestimate the equivalent crack depth, and a more accurate equivalent crack size can be obtained using the J-integral formula proposed.

Modified J Estimation by GE/EPRI Method for Circumferential Surface Cracked Pipes under Bending or Combined Bending and Pressure Loads

Development of J-Integral Solutions for Semi-Elliptical Circumferential Cracked Pipes Subjected to Internal Pressure and Bending Moment

A Strain-Based J-integral Formulation for an Internal Circumferential Surface Crack of Pipeline under Inner Pressure and Large Axial Deformation

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Empirical Correction Factor to Estimate the Plastic Collapse Bending Moment of Pipes with Circumferential Surface Flaw

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

Crack growth stability analysis method for LBB assessment technology in pressure vessels and pipes

Experimental Investigation of Failure Estimation Method for Circumferentially Cracked Pipes Subjected to Combined Bending and Torsion Moments

Experimental Investigation on the Limit Load Estimation Method for Pipes Containing a Circumferential Surface Flaw with Complicated Shape

Ductile Fracture Prediction Based on J-integral and Unified Constraint Parameters for Cracked Pipes

Engineering Estimation Method of Unified Constraint Parameters for Semi-Elliptical Surface Cracks in Plates

Using J-integral analysis to predict the failure of HDPE pipes under crack face load and internal pressure

Experimental Study on Failure Estimation Method for Circumferentially Cracked Pipes Subjected to Multi-Axial Loads

Numerical Simulation of Fatigue Life Prediction of Pressure Vessel Based on Cyclic J-integral

Fracture Estimation Method for Pipe with Multiple Circumferential Surface Flaws

Finite Element Analysis on the Mechanical Properties of the Combined Fittings With a Long Radius and Double Elbows

An approximative solution for limit load of piping branch junctions with circumferential crack and finite element validation

Empirical Solution of Stress Intensity Factors for the Inclined Inner Surface Crack of Pipe under External Pressure and Axial Compression

ICONE19-43138 Prediction of Failure Bending Moment for a Pipe Containing Multiple Circumferential Cracks with Complex Shapes

Experimental Verification on Limit Load Estimation Method for Pipes with an Arbitrary Shaped Circumferential Surface Flaw