Abstract:Flaws due to stress corrosion cracking have been detected in stainless steel or nickel-based alloy dissimilar metal weld joints of piping systems in nuclear power plants. Generally, stainless steel and nickel-based alloy are ductile materials with high toughness, and the failure mode of flawed pipes made of ductile materials is expected to be net-section plastic collapse. Failure bending moment of a ductile pipe containing a circumferential flaw is predicted using the net-section stress approach according to ASME Code Section XI as a limit load criterion. However, in the current code, the failure bending moment can only be adopted for a pipe containing a single circumferential flaw with constant depth, although many flaws detected actually are multiple flaws, and the flaw shapes are generally complex. In this study, a failure estimation method for pipes containing multiple circumferential flaws with complex shapes was proposed. Furthermore, failure experiments were performed for 8 inch diameter Schedule 80 stainless steel pipes containing two circular circumferential flaws. The failure bending moments obtained from the experiments were compared with the estimated results. Based on the experimental results, it was concluded that the proposed failure estimation method satisfactorily represents the failure behavior of the pipes and can be applied in engineering application.

Experimental Investigation on the Limit Load Estimation Method for Pipes Containing a Circumferential Surface Flaw with Complicated Shape

Experimental Verification on Limit Load Estimation Method for Pipes with an Arbitrary Shaped Circumferential Surface Flaw

Limit Load Estimation Method for Pipe with an Arbitrary Shaped Circumferential Surface Flaw

Failure Bending Moment for Pipes with an Arbitrary-Shaped Circumferential Flaw

Failure Bending Moment of Pipes Containing Multiple Circumferential Flaws with Complex Shape

Prediction of Failure Bending Moment for a Pipe with an Arbitrary-Shaped Circumferential Flaw

Prediction of Collapse Stress for Pipes with Arbitrary Multiple Circumferential Surface Flaws

Fracture Estimation Method for Pipe with Multiple Circumferential Surface Flaws

1003 Experimental Study on Limit Load Criterion for Pipe with Crack Modelled in Its Shape

Experimental Investigation on the Failure Estimation Method of Cracked Cylinders Subjected to Multi-Axial Loads

Experimental Investigation of Failure Estimation Method for Circumferentially Cracked Pipes Subjected to Combined Bending and Torsion Moments

Experimental Study on Failure Estimation Method for Circumferentially Cracked Pipes Subjected to Multi-Axial Loads

ICONE19-43138 Prediction of Failure Bending Moment for a Pipe Containing Multiple Circumferential Cracks with Complex Shapes

Research On Safety Assessment Method For Pressure Pipe With Incomplete Welding Defects Under Complicated Loadings

Plastic Limit Load Analysis for Pressure Pipe with Incomplete Welding Defects Based on the Extended Net Section Collapse Criteria

Limit bending moment for pipes with two circumferential flaws under combined internal pressure and bending

Failure Experiments on Pipes with Local Wall Thinning Subjected to Multi-Axial Loads

Empirical Correction Factor to Estimate the Plastic Collapse Bending Moment of Pipes with Circumferential Surface Flaw

Plastic Limit Load Analysis of Pressure Pipes Containing Incomplete Welding Defects under Combined Loadings

Allowable External Flaws and Acceptance Standards for High Toughness Ductile Pipes Subjected to Bending Moment and Internal Pressure

Failure Bending Stresses for Small Diameter Thick-Wall Pipes